供应PC(聚碳酸酯)L-1250Y/日本帝人注塑生产厂商：日本帝人化成公司特性备注：适宜于采用注坯吹塑成型用途：对流动性要求较高的薄壁制品、电器、电子元件、机械零件、劳保、医疗用品、照明器具及灯罩、餐具、容器。重要参数：密度:1.2 g/cm3吸水率:0.2 %成型收缩率:0.6 %拉伸强度:81 MPa断裂伸长率:140 %性能项目试验条件[状态]测试方法测试数据数据单位基本性能吸水率24hr，in 23℃ASTM D-5700.20%物理性能折射率 ASTM D-5421.585 透光率厚度3mmASTM D-100388%阻燃性厚度1.47mmUL 9494V-2 比重 ASTM D-7921.20 阻燃性厚度3.05mmUL 9494V-2 机械性能耐冲击强度值艾氏、带缺口厚度6.4mmASTM D-256140(14)j/m(kgf.cm/cm)洛氏硬度 ASTM D-78577M标度弯曲模量 ASTM D-7902230(22700)Mpa(kgf/cm2)拉伸强度屈服点 ASTM D-63861(620)Mpa(kgf/cm2)断裂点 ASTM D-63881(830)Mpa(kgf/cm2)耐冲击强度值艾氏、带缺口厚度3.2mmASTM D-256880(90)j/m(kgf.cm/cm)拉伸率屈服点 ASTM D-6386 断裂点 ASTM D-638140 弯曲强度 ASTM D-79090(915)Mpa(kgf/cm2)压缩强度 ASTM D-69576(770)Mpa(kgf/cm2)拉伸模量 ASTM D-6382120(21600)Mpa(kgf/cm2)电气性能介电正切60HzASTM D-1500.0004 体积电阻率 ASTM D-25731016Ω.cm绝缘破坏强度快速加压值厚度1.6mmASTM D-14930KV/mm介电正切106HzASTM D-1500.009 介电率60HzASTM D-1502.95 耐导电径迹性（CTI） IEC 112300V介电率106HzASTM D-1502.9 耐电弧性 ASTM D-495110secc加工性能成型收缩率流动方向 ASTM D-9550.5～0.7%垂直方向 ASTM D-9550.5～0.7%热性能线膨胀系数流动方向 ASTM D-696710-5cm/cm/℃垂直方向 ASTM D-696710-5cm/cm/℃负荷挠曲温度负荷0.451MPa(4.6kgf/cm)ASTM D-648143°C负荷挠曲温度负荷1.813MPa(18.6kgf/cm)ASTM D-648143°C温度指数电学式厚度1.47mmUL 746B125°C冲击式厚度1.47mmUL 746B115°C