光纤特性
衰减 | @1310nm | ≤3.5dB/km | ≤3.5dB/km | |
@1383nm | ≤3.5dB/km（after H2 aging) | ≤3.5dB/km（after H2 aging) | ||
@1460nm | ≤0.25dB/km | ≤0.23dB/km | ||
@1490nm |
|
| ||
@1550nm | ≤0.21dB/km | ≤0.21dB/km | ||
@1625nm | ≤0.23dB/km | ≤0.23dB/km | ||
相对波长的衰减变化 | @1310nm
@1550nm
| 1282~1330nm | ≤0.03dB/km | ≤0.03dB/km |
1525~1575nm | ≤0.02dB/km | ≤0.02dB/km | ||
波长范围内的色散 | 1285~1340nm @1550nm | -3.0~3.0[ps/(nm·km]≤18[ps/(nm·km] |
| |
@1625nm | ≤22[ps/(nm·km] |
| ||
零色散波长 | 1302~1322 nm·km | 1300~1324 nm·km | ||
令色散斜率 | ≤0.090 [ps/nm²·km] | ≤0.092 [ps/nm²·km] | ||
零色散率（经典值） | ≤0.090 [ps/nm²·km] |
| ||
偏振模色散系数（PMD) | 单根光纤最大值 | ≤0.2[ps/√km] | ≤0.2[ps/√km] | |
| Design link value(M=20, Q=0.01%) | ≤0.1[ps/√km] | ≤0.1[ps/√km] | |
光缆截止波长 | ≤1260nm | ≤1260nm | ||
模场直径 (MFD) | @1310nm | 9.6±0.4[μm] | 8.8±0.4[μm] | |
@1550nm | 10.1±0.5[μm] | 9.8±0.5[μm] | ||
有效群折射率 | @1310nm | 1.466 | 1.466 | |
@1550nm | 1.467 | 1.467 |
背向散射特性 (@1310nm/1550nm) (@1550nm)
台阶（双向平均值） | ≤0.05dB | ≤0.05dB |
不匀称性（整个光纤长度）和衰减不连续性 | ≤0.05dB | ≤0.05dB |
背向散射衰减系数差异 | ≤0.03[dB/km] | ≤0.03[dB/km] |
几何特性
包层直径 | 124.80±0.7[μm] | 124.80±0.7[μm] |
包层不圆度 | ≤1.0% | ≤0.7% |
涂层直径 | 245±7μm | 245±5μm |
涂层 /包层 同心度误差 | ≤12.0μm | ≤12.0μm |
涂层不圆度 | ≤6.0% | ≤6.0% |
芯/包层同心度误差 | ≤6.0μm | ≤6.0μm |
翘曲度（半径） | ≥4m | ≥4m |
环境特性(@1310nm/@1550nm)
温度附加衰减 ( -60s℃~+85℃） | ≤0.05dB/km | ≤0.05dB/km |
温度-湿度循环附加衰减 (-10℃~+85℃，98%R.H.) | ≤0.05dB/km | ≤0.05dB/km |
加速老化附加衰减 （85℃，85%相对湿度，30天） | ≤0.05dB/km | ≤0.05dB/km |
浸水附加衰减 (23℃,30days) | ≤0.05dB/km | ≤0.05dB/km |
机械特性
筛选张力 | 离线 | ≥9.0 N 9≥100kpsi） |
宏弯附加衰减（@1550nm)
| 1turn ,15mm diameter 1turn ,20mm diameter
| ≤1.0dB
|
| 10turn ,30mm diameter
| ≤1.0dB
|
| 100turn ,50mm diameter
| ≤0.05dB
|
涂层剥离力（经典值）
| 1.7 N | 1.7 N |
动态疲劳参数（nd，典型值) | ≥20 | ≥20 |