性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度) ASTM D638/ISO 52756.8（55.3）kg/cm²(MPa)[Lb/in2]断裂伸长率 ASTM D638/ISO 527--%拉伸模量 ASTM D638/ISO 5272310kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率) ASTM D638/ISO 5275.4%拉伸断裂伸长率(延伸率) ASTM D638/ISO 527110%弯曲模量(弯曲弹性率) ASTM D790/ISO 1782180（2120）kg/cm²(MPa)[Lb/in2]弯曲强度 ASTM D790/ISO 17892（89）kg/cm²(MPa)[Lb/in2]洛氏硬度 ASTM D785L-87 IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 179824kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179712kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 17965kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 17955kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 17970kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 17960kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179无断裂kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179无断裂kg·cm/cm(J/M)ft·lb/in物性性能比重（密度） ASTM D792/ISO 11831.19 成型收缩率 ASTM D9550.40-0.80%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 1133300℃.1.2kg,10g/10min220℃/10kgASTM D1238/ISO 1133--g/10min吸水率 23℃/24H ASTM D570/ISO 620.12%热性能热变形温度退火ASTM D648/ISO 75--℃（℉）未退火ASTM D648/ISO 751.80MPa/3.20mm,121℃，6.40mm,116℃℃（℉）维卡软化点 ASTM D1525/ISO R306138-139℃（℉）熔点 - ℃（℉）燃烧性（率） UL940.800mm,UL94HB;3.00mm,UL94V-2; 线性膨胀系数 ASTM D696/ISO 113590.000067-0.000080mm/mm.℃电气性能介电常数100HZASTM D150/IEC 60250-- 1MHZASTM D150/IEC 60250-- 介电损耗100HZASTM D150/IEC 60250-- 1MHZASTM D150/IEC 60250-- 体积电阻率 ASTM D257/IEC 600931.0E+15 ohm cmΩ.cm表面电阻率 ASTM D257/IEC 60093>1.0E+15 ohmsΩ耐电弧性 ASTM D495/IEC 60112-- 光学性能折射率 ASTM D542/ISO 489-- 透光率 ASTM D1003/ISO 1346882.0%模糊系数（Haze） ISO 147823.0%加工条件干燥条件 加工温度射嘴 ℃料筒前段 ℃料筒中段 ℃料筒后段 ℃熔体温度 ℃模具温度 ℃压力注塑压力 Mpa保压压力 Mpa背压 Mpa螺杆转速 rpm其他备注注射成型颜色透明特性共聚物，流动性中等，良好的加工性，成型周期快，延展性用途