Properties

性能

Test Method

测试方法

Resin-5333A

树脂-5333A

Hardener-5333B

固化剂-5333B

Mixed-A/B

混合物-A/B

Color/Appearance

颜色/外观

Visual

目测法

transparentliquid无色液体

transparent

liquid无色液态

transparent

无色透明

Specific Gravity

比重

ASTM D-792

1.15-1.18

0.98

Viscosity @ 25°C, cps粘度（25°C）

ASTM D-2393

11,000-13,000

10 - 14

2500 -3000

Shelf life, 25°C, month保质期，月

12

12

Property性能

Test Method测试方法

value数值

Hardness (Shore D)硬度

ASTM D-2240

86

Elongation at break断裂延伸率，%

3

Tensile strength拉伸强度,psi

9000

Glass transition temperature

玻璃化转变温度, Tg, ºC

DMA

80

Thermal Conductivity导热率, W/M-K

0.18

Max. service temperature最大工作温度, ºC

120

Coefficient of thermal expansion

热膨胀系数, CTE

ASTM D3386

68 E-06

Water absorption吸水率,% weight

0.15

Surface resistivity表面电阻, ohms

2.8E14

Volume resistivity体积电阻率, ohms-cm

3.0E16

Dielectric constant介电常数，1 kHz

ASTM D150

3.8

Dissipation factor耗散因子，Hz

0.013

Dielectric strength, KV/mm,介电强度

ASTM D149

60

Resin/Hardener Ratio (by weight) 树脂与固化剂重量比

100 / 12.5

Pot Life (200 gram mass), 25°C, minutes保质期（200g）25°C，分钟

60

Temperature温度

Minimum Cure Time最少固化时间

25 ºC (77ºF)

3 hours to handling strength 3小时到达操作强度

25 ºC (77ºF)

24 hours 24小时to full strength

60 ºC (158ºF)

3 hours 3小时