Properties

性能

Test Method

测试方法

Resin-5323A

树脂-5323A

Hardener-5323B

固化剂-5323B

Mixed-A/B

混合物-A/B

Color/Appearance

颜色/外观

Visual

目测法

Grey/black liquid灰黑色液体

Light colored liquid

浅色液态

Grey / black

灰黑

Specific Gravity

比重

ASTM D-792

1.58

0.98

Viscosity @ 25°C,

cps粘度（25°C）

ASTM D-2393

40,000-45,000

10 - 14

20,000-25,000

Shelf life, 25°C,

month保质期，月

12

12

Property性能

Test Method测试方法

value数值

Hardness (Shore D)硬度

ASTM D-2240

80

Elongation at break断裂延伸率，%

4

Tensile strength拉伸强度,psi

7500

Glass transition temperature

玻璃化转变温度, Tg, ºC

DMA

70

Thermal Conductivity导热率, W/M-K

0.47

Max. service temperature最大工作温度, ºC

120

Coefficient of thermal expansion

热膨胀系数, CTE

ASTM D3386

90 E-06

Water absorption吸水率,% weight

0.08

Surface resistivity表面电阻, ohms

1.0E14

Volume resistivity体积电阻率, ohms-cm

2.0E13

Dielectric constant介电常数，1 kHz

ASTM D150

4.9

Dissipation factor耗散因子，10kHz

0.07

Dielectric strength, KV/mm,介电强度

ASTM D149

30

Resin/Hardener Ratio (by weight) 树脂与固化剂重量比

100 / 6

Pot Life (200 gram mass), 25°C, minutes操作时间（200g）25°C,分钟

40-60

Temperature温度

Minimum Cure Time最少固化时间

25 ºC (77ºF)

3 hours to handling strength 3小时到达操作强度

25 ºC (77ºF)

24 hours 24小时

60 ºC (158ºF)

3 hours 3小时