供应台湾长春 PBT 4815 玻纤增强。阻燃级，电器开关及餐具手柄料
'
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 吸水率 | | ASTM D-570 | 0.03 | % |
| 物理性能 | 玻璃纤维含量 | | Ash | 15 | % |
| 比重 | | ASTM D-792 | 1.43-1.52 | |
| 成型收缩率 | | ASTM D-955 | 0.4-2.0 | % |
| 机械性能 | 引张伸长率 | | ASTM D-638 | 4-5.5 | % |
| 挠曲强度 | | ASTM D-790 | 1400-1800 | Kg/cm2 |
| 洛氏硬度 | | ASTM D-785 | 93 | M-Scale |
| IZOD冲击强度 | | ASTM D-256 | 5-7 | Kg.cm/cm |
| 挠曲弹性率 | | ASTM D-790 | 45000-65000 | Kg/cm2 |
| 引张强度 | | ASTM D-638 | 900-1100 | Kg/cm2 |
| 电气性能 | 绝缘破坏强度 | | ASTM D-149 | 22 | KV/mm |
| 耐电弧性 | | ASTM D-495 | 90 | sec |
| 诱电正接 | 60Hz | ASTM D-150 | 0.001 | |
| 诱电率 | 60Hz | ASTM D-150 | 3.3 | |
| 表面电阻率 | | ASTM D-257 | >1014 | Ω |
| 体积电阻率 | | ASTM D-257 | >1016 | Ω.cm |
| 热性能 | 耐燃性 | 3.0mm | UL 94 | V-0 | |
| 热变形温度 | 18.6Kg/cm2 | ASTM D-648 | 205 | ℃ |
| 熔点 | | DSC | 225 | ℃ |
| 线膨胀系数 | | ASTM D-696 | 5.5 | 10-5cm/cm℃ |
| 热变形温度 | 4.6Kg/cm2 | ASTM D-648 | 220 | ℃ |