韩国巴斯夫ABS GP-22
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 模塑收缩率(12×15×10mm) | | ASTM D-955(DIN16901) | 0.3-0.6 | % |
| 比重 | | ASTM D-792(ISO1183) | 10.4 | g/cm3 |
| 熔体流动速率 | 220℃ 10kg | ASTM D-1238(ISO1133) | 20 | g/10min |
| 吸水性 | | ASTM D-570(DIN53495-1L) | 0.3 | % |
| 阻燃性 | | UL-94 | HB |
| 熔体流动速率 | 200℃ 5kg | ASTM D-1238(ISO1133) | 1.6 | g/10min |
| 伸长率(屈服) | | ASTM D-638(ISO527-2) | 2.7 | % |
| 伸长率(断裂) | | ASTM D-638(ISO527-2) | 20 | % |
| 悬臂梁缺口冲击强度 | 23℃(-30℃) | ISO180/1U | 25(8) | KJ/m2 |
| 洛氏硬度 | | ASTM D-785 | 103 | R |
| 悬臂梁缺口冲击强度 | 3.2mm 23℃(3.2mm -30℃) | ASTM D-256 | 350(100) | J/m |
| 拉伸模量 | | ASTM D-638(ISO527-2) | 23500 | kg/cm2 |
| 简支梁冲击强度 | 23℃(-30℃) | ISO179/1eU | 210(110) | KJ/m2 |
| 弯曲模量 | | ASTM D-790(ISO178) | 24000 | kg/cm2 |
| 悬臂梁冲击强度 | 23℃(-30℃) | ISO180/1U | 150-n.b.(90) | KJ/m2 |
| 拉伸强度(屈服) | | ASTM D-638(ISO527-2) | 470 | kg/cm2 |
| 拉伸强度(断裂) | | ASTM D-638(ISO527-2) | 430 | kg/cm2 |
| 弯曲强度 | | ASTM D-790(ISO178) | 700 | kg/cm2 |
| 简支梁缺口冲击强度 | 23℃(-30℃) | ISO179/1eU | 23(8) | KJ/m2 |
| 线性膨胀系数 | | DIN53752 | 8-11 | (1K)×10-5 |
| 最大允许工作温度 | | | 80 | ℃ |
| 热变形温度 | 1.8MPa(HDT A) | ASTM D-648 | 101 | ℃ |
| 热传导性能 | -40℃-80℃ | DIN52612 | 0.17 | W/K.m |
| 热变形温度 | 0.45MPa(HDT B) | ASTM D-648 | 104 | ℃ |
| 维卡软化点 | | ISO306 | 97 | ℃ |