美国杜邦 408L PA66
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 吸水率 | 24hr | ASTM D-570 | 1.2 | % |
| 阻燃性 | | UL 94 | DAM｜50%RH,0.81｜- | mm |
| 比重 | | ASTM D-792 | DAM｜50%RH,1.09｜- |
| 模具收缩率 | 3.2mm | | DAM｜50%RH,1.5｜- | % |
| 阻燃性 | | UL 94 | HB |
| 断裂伸长率 | | ASTM D-638 | DAM｜50%RH,80｜270 | % |
| 屈服伸长率 | | ASTM D-638 | DAM｜50%RH,5｜15 | % |
| IZOD冲击强度 | | ASTM D-256 | DAM｜50%RH,229｜240 | J/m |
| 弯曲模量 | | ASTM D-790 | DAM｜50%RH,1965｜1103 | MPa |
| 拉伸屈服强度 | | ASTM D-638 | DAM｜50%RH,60.7｜5.17 | MPa |
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜50%RH,60.7｜51.7 | MPa |
| 体积电阻率 | | ASTM D-257 | DAM｜50%RH,10,15,｜10,13 | Ω.cm |
| 热变形温度 | 0.45MPa | ASTM D-648 | DAM｜50%RH,227｜- | ℃ |
| 热变形温度 | 1.80MPa | ASTM D-648 | DAM｜50%RH,75｜- | ℃ |
| 熔点 | | ASTM D-3418 | DAM｜50%RH,263｜- | ℃ |
| CLTE | | ASTM D-696 | DAM｜50%RH,0.81｜- | 10-4/K |