ABS/沙伯基础(原GE)/EX39
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体体积流率 | 220℃/10.0kg | ASTM D-1238 | 4.00 | g/10min |
| 比重 | ASTM D-7921.03g/cm3 |
| 模具收缩率 | Flow 3.20mm | ASTM D-955 | 0.70-0.90 | % |
| 拉伸模量 | ASTM D-6381680MPa |
| 拉伸屈服强度 | ASTM D-63835.9MPa |
| 拉伸断裂强度 | ASTM D-63829.0MPa |
| 拉伸屈服伸长率 | ASTM D-6383.5% |
| 拉伸断裂伸长率 | ASTM D-638110% |
| 弯曲模量 | 50.0mm Span | ASTM D-790 | 1900 | MPa |
| 弯曲屈服强度 | 50.0mm Span | ASTM D-790 | 57.9 | MPa |
| IZOD缺口冲击强度 | -30℃ | ASTM D-256 | 320 | J/m |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 465 | J/m |
| 热变形温度 | 0.45MPa,未退火,3.20mm | ASTM D-648 | 91.7 | ℃ |
| 热变形温度 | 1.80MPa,未退火,3.20mm | ASTM D-648 | 77.8 | ℃ |
| 维卡软化温度 | ASTM D-152595.0℃ |
| CLTE | Flow -40TO40℃ | ASTM E-831 | 0.00010 | cm/cm/℃ |
| CLTE | Transverse -40TO40℃ | ASTM E-831 | 0.00012 | cm/cm/℃ |
| 燃烧性 | 1.52mm | UL 94 | HB |