供应苏州欧太龙316Ti/0Cr18Ni12Mo2Ti不锈钢
| 316Ti是在SUS316钢中添加Ti来改善抗晶间腐蚀性能。 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 中国牌号 |
0Cr18Ni12Mo2Ti |
|
|
|
|
|
|
|
|
|
| 化学成分 |
|
|
|
|
机械性能 |
|
|
|
|
|
|
| C |
Si |
Mn |
P |
|
状 态 |
σ0.2[MPA] |
σb[MPA] |
δ5 [%] |
φ [%] |
HBS |
HRC |
| ≤0.08 |
≤1.00 |
≤2.00 |
≤0.045 |
|
固熔 |
≥205 |
≥530 |
≥40 |
≥55 |
≤187 |
≤90 |
| S |
Ni |
Cr |
Ti |
|
|
|
|
|
|
|
|
| ≤0.030 |
10.00-14.00 |
16.00-18.00 |
5*C%-0.70 |
|
|
|
|
|
|
|
|
| Mo |
其他 |
- |
- |
|
|
|
|
|
|
|
|
| 2.00-3.00 |
- |
- |
- |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 美国牌号 |
ASTM S31635 |
AISI 316Ti |
|
|
|
|
|
|
|
|
| 化学成分 |
|
|
|
|
|
|
|
|
|
|
|
| C |
Si |
Mn |
P |
|
|
|
|
|
|
|
|
| ≤0.08 |
≤1.00 |
≤2.00 |
≤0.045 |
|
|
|
|
|
|
|
|
| S |
Ni |
Cr |
Ti |
|
|
|
|
|
|
|
|
| ≤0.030 |
10.0-14.0 |
16.5-18.5 |
5*(C+N)-0.70 |
|
|
|
|
|
|
|
|
| Mo |
N |
- |
- |
|
|
|
|
|
|
|
|
| 2.00-3.00 |
0.1 |
- |
- |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 日本牌号 |
SUS316Ti |
|
|
|
|
|
|
|
|
|
|
| 化学成分 |
|
|
|
|
机械性能 |
|
|
|
|
|
|
| C |
Si |
Mn |
P |
|
σ0.2[MPA] |
σb[MPA] |
δ5 [%] |
φ [%] |
HRB |
HB |
HV |
| ≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
|
≥205 |
≥520 |
≥40 |
≥50 |
≤90 |
≤187 |
≤200 |
| S |
Ni |
Cr |
Ti |
|
|
|
|
|
|
|
|
| ≤0.030 |
11.0-14.0 |
16.0-18.0 |
≥5*C% |
|
|
|
|
|
|
|
|
| Mo |
其他 |
- |
- |
|
|
|
|
|
|
|
|
| 2.00-3.00 |
- |
- |
- |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 欧洲牌号 |
X6CrNiMoTi17-12-2 |
|
|
|
|
|
|
|
|
|
|
| 化学成分 |
|
|
|
|
机械性能 |
|
|
|
|
|
|
| C |
Si |
Mn |
P |
|
σ0.2[MPA] |
σb[MPA] |
δ5 [%] |
φ [%] |
HRB |
HB |
|
| ≤0.08 |
≤1.00 |
≤2.00 |
≤0.045 |
|
≥215 |
500-730 |
≥35 |
≥50 |
- |
130-190 |
|
| S |
Ni |
Cr |
Ti |
|
|
|
|
|
|
|
|
| 0.015-0.030 |
10.50-13.50 |
16.50-18.50 |
5*C-0.70 |
|
|
|
|
|
|
|
|
| Mo |
N |
- |
- |
|
|
|
|
|
|
|
|
| 2.00-2.50 |
0.11 |
- |
- |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 应用领域 |
|
|
|
|
|
|
|
|
|
|
|
|
广泛用于石油，化工，轻工，食品，化肥，纺织造纸，原子能等。 |
|
|
|
|
|
|
|
|
|