ABS 韩三星毛织 VE-0812 BK 物性认证数据表
-
| 性能项目 |
测试条件 |
测试方法 |
数值/描述 |
单位 |
| 机械性能 |
拉伸强度(引张强度) |
|
ASTM D638/ISO 527 |
10 |
kg/cm²(MPa)[Lb/in2] |
| 断裂伸长率 |
|
ASTM D638/ISO 527 |
15 |
% |
| 拉伸模量 |
|
ASTM D638/ISO 527 |
|
kg/cm²(MPa)[Lb/in2] |
| 拉伸屈服伸长率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
| 拉伸断裂伸长率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
| 弯曲模量(弯曲弹性率) |
|
ASTM D790/ISO 178 |
2300 |
kg/cm²(MPa)[Lb/in2] |
| 弯曲强度 |
|
ASTM D790/ISO 178 |
55 |
kg/cm²(MPa)[Lb/in2] |
| 洛氏硬度 |
|
ASTM D785 |
98 |
|
| IZOD 缺口冲击强度 |
1/4" 23℃ |
ASTM D256/ISO 179 |
|
kg
·cm/cm(J/M)ft
·lb/in |
| 1/4" -30℃ |
ASTM D256/ISO 179 |
|
kg
·cm/cm(J/M)ft
·lb/in |
| 1/8" 23℃ |
ASTM D256/ISO 179 |
|
kg
·cm/cm(J/M)ft
·lb/in |
| 1/8" -30℃ |
ASTM D256/ISO 179 |
|
kg
·cm/cm(J/M)ft
·lb/in |
| Charpy冲击强度 |
23℃ （缺口） |
ASTM D256/ISO 179 |
167 |
kg
·cm/cm(J/M)ft
·lb/in |
| -30℃（缺口） |
ASTM D256/ISO 179 |
|
kg
·cm/cm(J/M)ft
·lb/in |
| 23℃（无缺口） |
ASTM D256/ISO 179 |
|
kg
·cm/cm(J/M)ft
·lb/in |
| -30℃（无缺口） |
ASTM D256/ISO 179 |
|
kg
·cm/cm(J/M)ft
·lb/in |
| 物性性能 |
比重（密度） |
|
ASTM D792/ISO 1183 |
1.19 |
|
| 成型收缩率 |
|
ASTM D955 |
|
% |
| 熔融指数（流动系数） |
200℃/5kg |
ASTM D1238/ISO 1133 |
3.4 |
g/10min |
| 220℃/10kg |
ASTM D1238/ISO 1133 |
|
g/10min |
| 吸水率 23℃/24H |
|
ASTM D570/ISO 62 |
|
% |
| 热性能 |
热变形温度 |
退火 |
ASTM D648/ISO 75 |
|
℃（℉） |
| 未退火 |
ASTM D648/ISO 75 |
178 |
℃（℉） |
| 维卡软化点 |
|
ASTM D1525/ISO R306 |
198 |
℃（℉） |
| 熔点 |
|
- |
|
℃（℉） |
| 燃烧性（率） |
|
UL94 |
v-0 |
|
| 线性膨胀系数 |
|
ASTM D696/ISO 11359 |
|
mm/mm.℃ |
| 加工条件 |
干燥条件 |
|
|
|
|
| 加工温度 |
射嘴 |
|
|
℃ |
| 料筒前段 |
|
|
℃ |
| 料筒中段 |
|
|
℃ |
| 料筒后段 |
|
|
℃ |
| 熔体温度 |
|
|
|
℃ |
| 模具温度 |
|
|
|
℃ |
| 压力 |
注塑压力 |
|
|
Mpa |
| 保压压力 |
|
|
Mpa |
| 背压 |
|
|
Mpa |
| 螺杆转速 |
|
|
|
rpm |
| 其他 |
备注 |
|
| 颜色 |
|
| 特性 |
|
| 用途 |
|