铝合金:A5056W  A5083BD  A5083W  A6061BD  A6061W  A7075BD  A1085P  A1080P  A1070P  A1050P  A1100P  A1200P  A1N00P  A1N30P  A2014P  A2017P  A2219P  A2024P  A3003P  A3203P  A3004P  A3104P  A3005P  A3105P  A5005P  A5052P  A5652P  A5052P  A5154P  A5454P  A5082P  A5182P  A5083P  A5083PS  A5086P  A5N01P  A6061P  A6061P  A7075P  A7N01P  Al-Zn6-MgCu  Al-Cu4-SiMn  Al-Cu4Mg1  Al-Cu2Mg  Al-Mg1SiCu  3522AlCu4MgTi  R164AlCu4MgTi  R2147AlCu4MgTi  3522AlCu4NiMg2  R164AlCu4Ni2Mg2  3522AlSi5Cu3Mn  3522AlSiCu4  3522AlSiCu4Mn  R164AlSi5Cu3  R164AlSi5Cu3Fe  R164AlSi6Cu4  3522AlSi5Cu3  3522AlSi5Cu3Mn  3522AlSi5Cu4  3522AlSiCu4Mn  R164AlSi5Cu3  R164AlSi5Cu3Fe  R164AlSi6Cu4  3522AlSi5Cu1Mg  R164AlSi5Cu  3522AlSi7Mg  R214AlSi7Mg  3522AlSi10Mg  R164AlSi10Mg  R2147AlSi10Mg  3522AlSi8Cu3Fe  R164AlSi8Cu3Fe  3522AlSi12CuFe  3522AlSi8Cu3Fe  3522AlSi12Fe  R164AlSi12Cu  R164AlSi12Fe  R2147AlSi12  3522AlSi5  R164AlSi5  R164AlSi5Fe  3522AlMg3  R164AlMg3  R2147AlMg3  3522AlMg10  R164AlMg10  R2147AlMg3  3522AlMg10  R164AlMg10  R2147AlMg10  3255AlSi5  R164AlSi5  R164AlSi5Fe  3522AlMg3  R164AlMg3  R2147AlMg3  3522AlMg10  R164AlMg3  R2147AlMg10  Al99.0Cu  Al-Zn6-Mg-Cu  Al-Cu4-Mg1  Al-Cu4-Mg-Si  Al-Mg1-Si-Cu  Al-Mg0.5-Si  Al-Si-Mg-Mn  Al-Si1-Mg  Al-Mg4.5-Mn  Al-Mg4  Al-Mg3  A03830  A13800  A23900  A14130  A13500

1070铝板介绍

材料名称：1070纯铝

标准：GB/T3190-1996主要特征及应用范围：1070铝板具有塑性高，耐蚀，导电性和导热性好的特点，但强度低，不通过热处理强化，切削性不好，可接受接触焊，气焊。多利用其优点制造一些具有特定性能的结构件，如铝箔制成垫片及电容器，电子管隔离网，电线，电缆的防护套，网，线芯及飞机通风系统零件及装饰件。

化学成分：

硅Si：0.20

铁Fe: 0.25

铜Cu：0.04

锰Mn：0.03

镁Mg：0.03

锌Zn：0.04

钛Ti：0.03

钒V：0.05

铝Al：99.7

力学性能：

抗拉强度 σb (MPa) )≥75

条件屈服强度 σ0.2 (MPa) )≥35

试样尺寸：所有壁厚

注：板材室温横向力学性能

热处理工艺：　　进行油淬火回火。这类钢丝的强度不如铅浴处理的钢丝，但性能均匀一致，成本较低。冷卷成形后，进行去应力处理。拔到规定尺寸，再进行退火处理。软化后的冷卷成形后，需经过淬火+中温回火后才能获得所需的力学性能。