| 与典型值比较查找替代品添加到“我的材料” PDF 数据表电子邮件打印联系 UL IDES
|
| 所有数据一般信息物理性能力学性能热性能电气性能与可燃性加工信息 | 单位 英制 | 公制 |
|
| 产品说明 | ||||
Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffness, balanced properties in flow, impact and heat designed for various thin wall applications. | ||||
| 总体 | ||||
材料状态 |
| |||
资料 1 |
| |||
搜索 UL 黄卡 |
| |||
供货地区 |
| |||
填料/增强材料 |
| |||
添加剂 |
| |||
性能特点 |
| |||
用途 |
| |||
加工方法 |
| |||
| 物理性能 | 额定值 | 单位制 | 测试方法 |
比重 | |||
-- | 1.26 | g/cm | ASTM D792 |
-- | 1.25 | g/cm | ISO 1183 |
熔流率 (260°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
溶化体积流率（MVR） (220°C/5.0 kg) | 14.0 | cm/10min | ISO 1133 |
收缩率 | Internal Method | ||
流动: 3.20 mm | 0.30 到 0.50 | % | |
横向流动: 3.20 mm | 0.40 到 0.60 | % | |
吸水率 | |||
24 hr, 50% RH | 0.010 | % | ASTM D570 |
24 hr | 0.10 | % | ASTM D570 |
饱和, 23°C | 0.090 | % | ISO 62 |
平衡, 23°C, 50% RH | 0.010 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | |||
-- 2 | 3500 | MPa | ASTM D638 |
-- | 3200 | MPa | ISO 527-2/1 |
抗张强度 | |||
屈服 3 | 65.0 | MPa | ASTM D638 |
屈服 4 | 65.0 | MPa | ASTM D638 |
断裂 3 | 50.0 | MPa | ASTM D638 |
断裂 | 50.0 | MPa | ISO 527-2/5 |
伸长率 | |||
屈服 3 | 4.0 | % | ASTM D638 |
屈服 | 3.5 | % | ISO 527-2/5 |
断裂 3 | 100 | % | ASTM D638 |
断裂 | 15 | % | ISO 527-2/50 |
弯曲模量 | |||
50.0 mm 跨距 5 | 3300 | MPa | ASTM D790 |
-- 6 | 3450 | MPa | ISO 178 |
弯曲强度 | |||
-- 6, 7 | 97.0 | MPa | ISO 178 |
屈服, 50.0 mm 跨距 5 | 100 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度 8 | ISO 179/1eA | ||
-30°C | 5.0 | kJ/m | |
23°C | 10 | kJ/m | |
悬壁梁缺口冲击强度 | |||
-30°C | 88 | J/m | ASTM D256 |
23°C | 200 | J/m | ASTM D256 |
-30°C 9 | 5.0 | kJ/m | ISO 180/1A |
23°C 9 | 10 | kJ/m | ISO 180/1A |
装有测量仪表的落镖冲击 (23°C, Total Energy) | 50.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度 | |||
0.45 MPa, 未退火, 6.40 mm | 97.0 | °C | ASTM D648 |
1.8 MPa, 未退火, 3.20 mm | 83.0 | °C | ASTM D648 |
1.8 MPa, 未退火, 6.40 mm | 89.0 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 10 | 80.0 | °C | ISO 75-2/Af |
维卡软化温度 | |||
-- | 91.0 | °C | ASTM D1525 11 |
-- | 98.0 | °C | ISO 306/B50 |
-- | 102 | °C | ISO 306/B120 |
Ball Pressure Test (75°C) | Pass |
| IEC 60695-10-2 |
线形膨胀系数 | ASTM E831, ISO 11359-2 | ||
流动: -40 到 40°C | 0.000055 | cm/cm/°C | |
横向: -40 到 40°C | 0.000060 | cm/cm/°C |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
表面电阻率 | 3.5E+15 | ohm | ASTM D257 |
体积电阻率 | 2.7E+16 | ohm·cm | ASTM D257 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
UL 阻燃等级 | UL 94 | ||
0.600 mm | V-1 |
| |
0.800 mm | V-0 |
| |
1.50 mm | 5VB |
| |
灼热丝易燃指数 (0.800 mm) | 960 | °C | IEC 60695-2-12 |
热灯丝点火温度 | IEC 60695-2-13 | ||
1.00 mm | 850 | °C | |
3.00 mm | 800 | °C |
| 注射 | 额定值 | 单位制 |
|
干燥温度 | 90.0 | °C | |
干燥时间 | > 4.0 | hr | |
建议的最大水分含量 | 0.040 | % | |
螺筒后部温度 | 275 到 300 | °C | |
螺筒中部温度 | 275 到 300 | °C | |
螺筒前部温度 | 280 到 300 | °C | |
射嘴温度 | 280 到 300 | °C | |
加工（熔体）温度 | 275 到 300 | °C | |
模具温度 | 60.0 到 80.0 | °C |
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
| 25.0 mm/min |
| 3类型 1, 5.0 mm/min |
| 4类型 1, 50 mm/min |
| 51.3 mm/min |
| 62.0 mm/min |
| 7Yield |
| 880*10*3 sp=62mm |
| 980*10*3 |
| 1080*10*4 mm |
| 11标准 B (120°C/h), 压 力2 (50N) |