供应PC/(聚碳酸酯#防弹胶)日本帝人 /LS-2250 吹塑 高韧性
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 吸水率 | 24hr in 23℃ | ASTM D-570 | 0.17 | % |
| 物理性能 | 透光率 | 3mm thick | ASTM D-1003 | Translucent | % |
| 比重 | | JIS K-7112 | 1.26 | |
| 阻燃性 | 1.5mm | UL 94 | V-2 | |
| 机械性能 | 拉伸模量 | | ASTM D-638 | 2300(23500) | Mpa(kgf/cm2) |
| 洛氏硬度 | | ASTM D-785 | 67 | M标度 |
| 拉伸强度 | 屈服点 | | ASTM D-638 | 55(560) | Mpa(kgf/cm2) |
| 断裂点 | | ASTM D-638 | 51(520) | Mpa(kgf/cm2) |
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 290(30) | J/m(kgf·cm/cm) |
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 120(12) | J/m(kgf·cm/cm) |
| 压缩强度 | | ASTM D-695 | 73(740) | Mpa(kgf/cm2) |
| 拉伸率 | 屈服点 | | ASTM D-638 | 78(800) | % |
| 断裂点 | | ASTM D-638 | 2110(21500) | % |
| 电气性能 | 耐导电径迹性（CTI） | | IEC 112 | 340 | V |
| 介电正切 | 60Hz | ASTM D-150 | 0.0008 | |
| 介电率 | 60Hz | ASTM D-150 | 2.85 | |
| 体积电阻率 | | ASTM D-257 | 3×1016 | Ω.cm |
| 介电正切 | 106Hz | ASTM D-150 | 0.008 | |
| 绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | kv/mm |
| 介电率 | 106Hz | ASTM D-150 | 2.8 | |
| 耐电弧性 | | ASTM D-495 | 100 | sec |
| 加工性能 | 成型收缩率 | 流动方向 | | ASTM D-955 | 0.5～0.7 | % |
| 垂直方向 | | ASTM D-955 | 0.5～0.7 | % |
| 热性能 | 负荷挠曲温度 | 负荷1.813MPa(18.6kgf/cm2) | JIS K-7207 | 136 | ℃ |
| 温度指数 | 电学式 | 厚度1.47mm | UL 746B | 115 | °C |
| 冲击式 | 厚度1.47mm | UL 746B | 105 | °C |
| 非冲击式 | 厚度1.47mm | UL 746B | 105 | °C |
| 负荷挠曲温度 | 负荷0.451MPa(4.6kgf/cm2) | JIS K-7207 | 145 | ℃ |
| 线膨胀系数 | 流动方向 | | ASTM D-696 | 7 | 10-5cm/cm/℃ |
| 垂直方向 | | ASTM D-696 | 7 | 10-5cm/cm/℃ |