阻燃级PC/940-701*940-701*940-701 欧盟GE PC940-701黑色粒子
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 吸水率 | | ASTM D-570 | 0.15 | % |
| 熔体流动速率 | | ASTM D-1238 | 17 | g/10min |
| 物理性能 | 阻燃性 | | UL 94 | 5V | |
| 阻燃性 | | UL 94 | 1.5 | mm |
| 阻燃性 | | UL 94 | 3.0 | mm |
| 比重 | | ASTM D-792 | 1.21 | |
| 模具收缩率 | 3.2mm | ASTM D-955 | 5-7 | 10-3 |
| 阻燃性 | | UL 94 | V-0 | |
| 机械性能 | 断裂伸长率 | | ASTM D-638 | 90 | % |
| 拉伸强度 | 屈服点 | | ASTM D-638 | 62 | MPa |
| 断裂点 | | ASTM D-638 | 56 | MPa |
| 弯曲模量 | | ASTM D-790 | 2239 | MPa |
| 缺口冲击强度 | 23°C | ASTM D-256 | 640 | J/m |
| 弯曲强度 | | ASTM D-790 | 91 | MPa |
| 洛氏硬度 | | ASTM D-785 | 118 | |
| 洛氏硬度 | | ASTM D785 | 70 | |
| 压缩强度 | | ADTM D695 | 12500 | psi |
| 压缩模量 | | ASTM D695 | 325000 | psi |
| 剪切强度 | | ASTM D732 | 10000 | psi |
| 剪切模量 | | ASTM D4065 | 114000 | psi |
| 疲劳极限 | 2.5MM循环 | ASTM D671 | 1000 | psi |
| 电气性能 | 体积电阻率 | | ASTM D-257 | 1.0×1017 | Ω.cm |
| 介电常数 | 1MHz | ASTM D-150 | 2.96 | |
| 介电常数 | 60Hz | ASTM D-150 | 3.01 | |
| 损耗因数 | 1MHz | ASTM D-150 | 0.01 | |
| 损耗因数 | 60Hz | ASTM D-150 | 0.0009 | |
| 加工性能 | 干燥温度 | | | 250 | deg F |
| 干燥时间 | 基本 | | 3-4 | h |
| 干燥时间 | 累积 | | 48 | h |
| 含湿量 | | | 0.02 | % |
| 熔体温度 | | | 560-600 | deg F |
| 注嘴温度 | | | 550-590 | deg F |
| 前段温度 | | | 560-600 | deg F |
| 中段温度 | | | 540-580 | deg F |
| 后段温度 | | | 520-560 | deg F |
| 模具温度 | | | 160-200 | deg F |
| 螺杆速度 | | | 40-70 | rpm |
| 机筒注射量 | | | 40-60 | % |
| 合模力吨数 | | | 3-5 | tons/psi |
| 排气槽深度 | | | 0.0010-0.0030 | in |
| 热性能 | 热变形温度 | 0.45MPa | ASTM D-648 | 137 | °C |
| UL长期使用温度 | | UL 746B | 120 | °C |
| 线膨胀系数 | | ASTM E-831 | 6.8×10-5 | 1/°C |
| 维卡软化点 | | ASTM D-1525 | 151 | °C |
| 热变形温度 | 1.8MPa | ASTM D-648 | 132 | °C |
| 其它性能 | 氧指数 | | ASTM D2863 | 35.0 | % |
产品细节图