供应 PMMA VR-L40 三菱丽阳 耐冲击材料 
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 成形收缩率 | ASTM D-9550.3-0.7% |
| 折射率 | ASTM D-5421.49nd |
| 吸水率 | 24hr | ASTM D-570 | 0.4 | % |
| 全光线透射系数 | 3.2mm | ASTM D-1003 | 92 | % |
| 比重 | ASTM D-7921.16 |
| 悬臂梁式冲击强度 | 1/4"付 | ASTM D-256 | 11 | kg.cm/cm |
| 弯曲弹性模量 | 1/4"棒 | ASTM D-790 | 2.0×104 | Kg/cm2 |
| 抗弯强度 | 1/4"棒 | ASTM D-790 | 630 | Kg/cm2 |
| 延展率 | ASTM NO.1 | ASTM D-638 | 80 | % |
| 抗拉强度 | ASTM NO.1 | ASTM D-638 | 430 | Kg/cm2 |
| 洛氏硬度 | M scale | ASTM D-785 | 67 |
| 介质损耗角正切 | 60HZ | JIS K-6911 | 0.04 |
| 体积电阻系数 | JIS K-6911>1015Ω.m |
| 耐电弧性 | JIS K-6911没有痕迹 |
| 介电常数 | 60Hz | JIS K-6911 | 3.9 | 60HZ |
| 表面电阻系数 | JIS K-6911>1016Ω |
| 绝缘击穿强度 | JIS K-691115kv/mm |
| 线膨胀系数 | ASTM D-6969×10-5cm/cm/℃ |
| 热传导系数 | ASTM C-1775×10-4cal/s/cm/°C |
| 比热 | 0.35cal/g/°C |
| 熔体流动性 | 230°C 3.8kg | ASTM D-1238 | 2.2 | g/10min |
| 载荷挠曲温度 | 18.56kg/cm2 | ASTM D-648 | 94 | °C |
| 维卡软化温度 | 1kg | ASTM D-1525 | 109 | °C |