汽车水室专用料,耐水解,30%玻纤增强PA66,可替代杜邦FR530
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 吸水率 | | ASTM D-570 | 0.05 | % |
| 物理性能 | 模具收缩率 | 3.2mm,flow | | 0.25 | % |
| 模具收缩率 | 1.57mm.flow | | 0.16 | % |
| 比重 | | ASTM D-792 | 1.67 | |
| 机械性能 | IZOD冲击强度 | -40℃ | ASTM D-256 | 80 | J/m |
| 弯曲强度 | 23℃ | ASTM D-790 | 200 | MPa |
| IZOD冲击强度 | 23℃ | ASTM D-256 | 91 | J/m |
| 无缺口冲击强度 | 23℃ | ASTM D-4812 | 585 | J/m |
| IZOD无缺口冲击强度 | -40℃ | ASTM D-4812 | 535 | J/m |
| 电气性能 | 介电常数 | 106 | ASTM D-150 | 3.7 | |
| 介电常数 | 103 | ASTM D-150 | 3.8 | |
| 介电强度 | 1.6mm | ASTM D-149 | 25.0 | kv/mm |
| 体积电阻率 | | ASTM D-257 | 1015 | Ω.cm |
| 抗电弧性 | | ASTM D-495 | 60-120 | S |
| 介电强度 | 3.2mm | ASTM D-149 | 18.0 | kv/mm |
| 表面电阻率 | | ASTM D-257 | 1014 | Ω |
| 损耗因数 | 106 | ASTM D-150 | 0.018 | |
| 损耗因数 | 103 | ASTM D-150 | 0.011 | |
| CTI | | UL 746A | 250-400 | V |
| 热性能 | 热变形温度 | 0.45MPa | ASTM D-648 | 246 | ℃ |
| 热变形温度 | 1.80MPa | ASTM D-648 | 224 | ℃ |