增韧尼龙 轴承保持架专用料 PA6 B601/南京德尔隆
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 饱和吸水率 | 24hr | ASTM D-570 | 8.5 | % |
| 吸水率 | | ASTM D-570 | 0.8 | % |
| 密度 | | ASTM D-792 | 1.1 | g/cm3 |
| 物理性能 | 线性成型收缩率 | | ASTM D-955 | 0.009-0.013 | mm/mm |
| 注塑成型温度范围 | | | 225-265 | ℃ |
| 烘干温度/时间 | | | 90/4-6 | ℃/hr |
| 机械性能 | 悬臂梁缺口冲击强度 | | ASTM D-256 | 13 | KJ/m2 |
| 屈服弯曲强度 | | ASTM D-790 | 80 | Mpa |
| 弯曲模量 | | ASTM D-790 | 2000 | Mpa |
| 断裂伸长率 | | ASTM D-638 | ＞35 | % |
| 断裂拉伸强度 | | ASTM D-638 | 65 | Mpa |
| 洛氏硬度 | | | R110 | |
| 电气性能 | 介电强度 | | ASTM D-149 | 20 | KV/mm |
| 表面电阻率 | | ASTM D-257 | 1013 | ohm |
| 热性能 | 熔点 | | | 220 | ℃ |
| 热变形温度 | 0.45MPa/1.81MPa | ASTM D-648 | 160/65 | ℃ |