乐泰3211
产品简介
乐泰产品3211 是一种单组分，触性胶粘剂，该产品暴露于足够强度的紫外线和/或可见光下就会快速固化形成柔韧透明的胶层。
典型用途
乐泰产品 3211 主要是为聚碳酸酯基材之间彼此粘接而设计的，并且在典型的模压应力水平下还不会产生应力开裂。它的柔韧特性提高了粘接面承受载荷的能力，改善了减震特性。另外本产品对大多数基材都表现出良好的粘接特性，包括玻璃，许多塑料和大多数金属。乐泰 3211 已经通过了 USP VI级认证。适用在一次性医用设备组装件上。
消毒的影响
与乐泰产品 3211 成分相似产品经过 E.T.O 或g辐射( 2.5 和 5.0 兆拉德 ) ，结果显示均具有优异的粘接强度保有率。 泰产品 3211 在121-127°F 蒸汽处理30分钟，1 个循环，结果显示具有优异的粘接强度保有率。这些产品不建议反复进行高压蒸消毒。
PRODUCT DESCRIPTION
LOCTITE® Product 3211 is a one component, thixotropic
adhesive which cures rapidly to form flexible, transparent
bonds when exposed to ultraviolet radiation and/or visible light
of sufficient intensity.
TYPICAL APPLICATIONS
Loctite Product 3211 is primarily designed for bonding
polycarbonate to itself, while not inducing stress cracking
under typical moulded in stress levels. Its flexibility enhances
the load bearing and shock absorbing characteristics of the
bond area. It has also shown excellent adhesion to a wide
variety of substrates including glass, many plastics and most
metals. Loctite 3211 has USP Class VI Certification. Suitable
for use in assembly of disposable medical devices.
PROPERTIES OF UNCURED MATERIAL
Typical
Value Range
Chemical Type Acrylated Urethane
Appearance Pale, yellow liquid
Specific Gravity @ 25°C 1.13
Viscosity @ 25°C, mPa.s (cP)
Brookfield RVTD
Spindle 4 @ 20 rpm 11,500 8,000 to 15,000
Refractive index, ND 1.48
Flash Point (), °C 80
Stress Cracking
Liquid adhesive was applied to a medical grade polycarbonate
bar 6.4cm by 13mm by 3mm which had been flexed to induce
different stress levels. The time it took for signs of crazing or
stress cracking to appear was recorded.
Stress Cracking, ASTM D3929 17 N/ mm2 >15 minutes
(2500 psi)
TYPICAL CURING PERFORMANCE
This product can be cured by irradiation with ultraviolet and/or
visible light of sufficient intensity. To obtain full cure on
surfaces exposed to air, the intensity of UV radiation at 220 to
260 nm will elerate the tack free cure of surface. The cure
rate and ultimate depth of cure will depend on light intensity,
the spectral distribution of the light source, the exposure time
and the light transmittance of the substrates.
NOTE: UV intensities where quoted are measured at
365nm using an OAI 306 UV Powermeter.
Depth of Cure vs. UV Irradiance
The graphs below show the increase in depth of cure with time
at 30 mW/cm2 - 100 mW/cm2 as measured from the thickness
of the cured pellet formed in a 15mm diameter PTFE die.
When exposed to a V Bulb at irradiances of 50 and 100
mW/cm2 for 30 seconds, a depth of cure greater than 13 mm
was achieved. The performance for Medium Pressure Hg will
be similar to Fusion H Bulb.
Hardness (Shore D): 51
Water absorption, ASTM D570, 2hrs in boiling water, % 2.72
Refractive index, ND 1.50
Electrical Properties Constant Loss
Dielectric constant & loss, ASTM D150 @ 100 Hz 5.697 0.0426
@ 1 kHz 5.605 0.0188
@ 1 MHz 5.131 0.0419
Volume resistivity, ASTM D149, W.cm 8.9 x 1014
Surface resistivity, ASTM D149, W 8.7 x 1014
Dielectric strength, ASTM D257, kV/mm 24
PERFORMANCE OF CURED MATERIAL
Shear strength in tensile mode tested in ordance with
ASTM D3163 on polycarbonate with a 0.5mm gap. Lap shear
assemblies were cured for 80 seconds @ 30mW/cm2 using a
metal halide light source.
Initial Strength, N/mm2 11
(psi) (1600)
TYPICAL ENVIRONMENTAL RESISTANCE
Test Procedure: ASTM D3163
Substrate: Polycarbonate with 0.5mm gap
Cure Procedure: 80 secs @ 30mW/cm2 Metal Halide
Solvent Temp. % of initial strength retained at
2hrs 24hrs 170hrs
Boiling Water 70
Water Immersion 49°C 60
Isopropanol immersion RT 95
Humidity Resistance 38°C 75
Heat Ageing on polycarbonate substrates
Temp. 170hrs 340hrs
Bonded polycarbonate 71°C 1001 1001
Bonded polycarbonate 93°C 1001 1001
Bonded polycarbonate 121°C 751 601
1Substrate failure
Effects of Sterilisation
Products similar in composition to Loctite 3211 subjected to
standard sterilisation by E.T.O. or Gamma Radiation (2.5 and
5.0 Megarads) show excellent bond strength retention. Loctite
3211 has shown excellent bond strength retention following
exposure to 121 - 127°C steam for 30 minutes, 1 cycle.
Repeated autoclaving is not mended with these
adhesives. It is mended that customers test specific
parts after subjecting them to preferred sterilisation method.
GENERAL INFORMATION
This product is not mended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidising materials.
Approvals
Product 3211 has been granted USP Class VI certification
which makes it particularly suited for use in disposable
medical device assemblies.
Directions for use
This product is UV sensitive. Exposure to daylight, UV light
and artificial lighting should be kept to a minimum during
storage and handling. Product should be dispensed from
applicators with black feed lines. For best performance bond
surfaces should be clean and free from grease. UV cure rate
is dependent on lamp intensity, distance from light source,
depth of cure needed or bondline gap and light transmittance
of the substrate through which the radiation must pass.
mended intensity for cure in bondline situation is 5
mW/cm2 minimum (measured at the bondline) with an
exposure time of 4-5 times the fixture time at this same
intensity. For dry curing of exposed surfaces higher intensity
UV is required (100 mW/cm2 minimum). Cooling should be
provided for temperature sensitive substrates such as
thermoplastics. Crystalline and semi-crystalline
thermoplastics should be checked for risk of stress cracking
when exposed to liquid adhesive. Excess adhesive can be
wiped away with organic solvent. Bonds should be allowed to
cool before subjecting to any service loads.
Storage
Product shall be ideally stored in a cool, dry location in
unopened containers at a temperature between 8°C to 28°C
(46°F to 82°F) unless otherwise labelled. Optimal storage is
at the lower half of this temperature range. To prevent
contamination of unused product, do not return any material to
its original container.
优势方面
我们只提供原装正品汉高乐泰、道康宁、3M、迈图等产品，我们为广大客户朋友提供极具竞争优势的价格。
汉高乐泰是全球胶粘剂技术和品牌市场领导者。
道康宁、迈图是全球硅胶领域的市场领导者。
3M是全球胶带、环氧胶、结构胶等领域的市场领导者。
我们是专业胶粘剂及施胶设备整体解决方案供应商，我们不止卖产品，我们更为客户提供全面而专业的售前指导和售后服务工作，直至广大客户的项目正常运转！
欲知更多产品详情，欢迎咨询深圳市鹏科泰贸易有限公司
网址：/
电话：0755-86381816 86381822
传真：0755-86381816