| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能熔体流动速率200℃×5kgf(49N)ASTM D-1238(ISO 1133)1.4g/10min |
| 熔体流动速率220℃×10kgf(98N)ASTM D-1238(ISO 1133)15g/10min |
| 物理性能比重23℃/23℃ASTM D-792(ISO 1183)1.04 |
| 机械性能弯曲模数23℃ASTM D-790(ISO 178)24000(2350)kg/cm2(MPa) |
| 拉伸强度23℃ASTM D-638(ISO 527)440(43)kg/cm2(MPa) |
| IZOD冲击强度23℃ASTM D-256(ISO R180)25(245)kg.cm/cm(J/m) |
| 弯曲强度23℃ASTM D-790(ISO 178)730(72)kg/cm2(MPa) |
| 洛氏硬度23℃ASTM D-785(ISO 2039/2)R-104 |
| 热性能维卡软化点1Kg loadASTM D-1525(ISO 306)102℃ |
| 热变形温度Annealed(8℃×8hr)ASTM D-648(ISO 75/A)99℃ |
| 热变形温度Unanneaied 18.6kg/cm²(1/2"厚）ASTM D-648(ISO 75/A)87℃ |