板 |
牌号 Grade | TA1,TA2,TA3, TA5,TA6,TA7,TA9,TA10,TC1,TC2,TC3,TC4 | Gr1,Gr2,Gr3,Gr4,Gr5,Ti6Al4V ELI,Gr7,Gr9,Gr11,G, Gr23 | 标准 Standard | GB/T3621-2007 | ASTM B265, ASME SB265,ASTM F136,ASTM F67,AMS4911,MIL9046, MIL9047 | 规格 Size | T 0.5-5.0mm x W1000mm x L 2000-3500mm T 6.0- 30mm x W1000-2500mm x L 3000-6000mm T 30- 80mm x W1000mm x L 2000mm | 应用领域 Applications | 医疗、航空、军工、石油化工、冶金、制盐、纺织、体育等行业。 | Medical, aviation, military, petrochemical engineering, metallurgy, salt-making, textile, sports and so on. |
Mechanical Requirements: Annealed-Sheet,Strip,and Plate (ASTM F67-06) Grade | Tensile Strength,min | Yield Strength, (0.2% Offset) | Elongation in 2 in. or 50mm, min,% | Bend Test Mandrel Diameter | ksi | MPa | min | max | Under 0.070 in. (1.8mm) in Thickness | 0.070 to 0.187 in.(1.8 to 4.75mm)in Thickness | ksi | MPa | ksi | MPa | 1 | 35 | 240 | 25 | 170 | 45 | 310 | 24 | 3T | 4T | 2 | 50 | 345 | 40 | 275 | 65 | 450 | 20 | 4T | 5T | 3 | 65 | 450 | 55 | 380 | 80 | 550 | 18 | 4T | 5T | 4 | 80 | 550 | 70 | 483 | 95 | 655 | 15 | 5T | 6T |
|
TA2
TA2的性能：
工业纯钛按其杂质含量的不同，分为TA1、TA2和TA3三个牌号。这三种工业纯钛的间隙杂质元素是逐渐增加的，故其机械强度和硬度也随之逐级增加，但塑性、韧性相应下降。
工业上常用的工业纯钛是TA2，因其耐蚀性能和综合力学性能适中。对耐磨和强度要求较高时可采用TA3。对要求较好的成型性能时可用TA1。
国标中的TA1，TA2和TA3对应这UNS中Gr0，Gr1和Gr2。
TA1、TA2在铁量ω为0.095%、氧含量ω为0.08%、氢含量ω为0. 0009%、氮含量ω为0.0062%时，具有很好的低温韧性和高的低温强度，可用作-253℃以下的低温结构材料。
TA2化学成分：
TA2含钛(Ti) 余量,铁(Fe)≤0.30,碳(C)≤0.10,氮(N)≤0.05,氢(H)≤0.015,氧(O)≤0.25。