DP 5080A]

	These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Impact properties: N = non-break, P = partial break, C = complete break

ISO Shortname: 

PropertyTest ConditionUnitStandardtypical Value

						drying according to specifications	annealed	-
Mechanical properties (23 °C/50 % r. h.)
	shore hardness, method A		-	ISO 868		80
	shore hardness, method D		-	ISO 868		29
	Ultimate tensile strength	200 mm/min	MPa	DIN 53504		23,8
	Strain at break	200 mm/min	%	DIN 53504		701
	Stress at 10 % strain	200 mm/min	MPa	DIN 53504		1,5
	Stress at 50 % strain	200 mm/min	MPa	DIN 53504		3,8
	Stress at 100 % strain	200 mm/min	MPa	DIN 53504		5,0
	Stress at 300 % strain	200 mm/min	MPa	DIN 53504		8,6
	Compression set	24 h; 70 °C	%	ISO 815		50
	Compression set	72 h; 23 °C	%	ISO 815		20
	Abrasion resistance		mm³	ISO 4649		70
	Impact resilience		%	ISO 4662		45
	Tear propagation resistance	500 mm/min	kN/m	ISO 34-1		55
Thermal properties
	Tensile storage modulus	-20 °C	MPa	ISO 6721-1,-4		105
	Tensile storage modulus	20 °C	MPa	ISO 6721-1,-4		31
	Tensile storage modulus	60 °C	MPa	ISO 6721-1,-4		23
Other properties (23 °C)
	Density		kg/m³	ISO 1183-1			1140
Molding conditions
	Injection molding-Melt temperature		°C	-	190 - 210
	Injection molding-Mold temperature		°C	-			20 - 40
	Maximum drying temperature		°C	-			80