美国诺誉化工,TPU,54605,5703,5714,58070,58132,58142
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTM D-792 | 1.19 | |
| 机械性能 | 100%模量伸长率 | | ASTM D-412（ASTM D-638） | 2.3 | MPa |
| 洛氏硬度 | | ASTM D-2240 | 70A | |
| Brookfield Viscosity | 15% T.S.in 80:20 MEK:TOL | | 250 | cps |
| Adhesion to PET | Cast in cyclohexanone | TP-141 | 0.12 | KN/m |
| 极限伸长率 | | ASTM D-412（ASTM D-638） | 630 | % |
| 拉伸强度 | | ASTM D-412（ASTM D-638） | 31.0 | MPa |
| 300%模量伸长率 | | ASTM D-412（ASTM D-638） | 3.8 | MPa |
| Brookfield Viscosity | 15% T.S.in cyclohexanone | | 1600 | cps |
| Adhesion to PET | Cast in MEK | TP-141 | 0.11 | KN/m |
| 热性能 | 玻璃化转变温度 | | DSC | -31 | ℃ |
| 其它性能 | T-peel,Aluminum Foil | | ASTM D-1876-72 | 1.8 | KN/m |
| Ring and Ball Softening Point | | ASTM E-28-92 | 179 | ℃ |
| Open Time | | ASTM D-4497-94 | ＞300 | sec |
| Melt Viscosity @ 204 C(400℃) | | ASTM D-1084-88 | 92000 | cps |
| Gradient Bar Tack Temperature | | | 91 | ℃ |
| T-peel,Mylar Film | | ASTM D-1876-72 | 3.4 | KN/m |