电话插头 电子插件 外壳 PC 301V-10 韩国LG-DOW
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTM D792 | 1.20 | g/cm3; |
| | 熔流率 | 300°C/1.2 kg | ASTM D1238 | 10 | g/10 min |
| | 收缩率 | 流动 | ASTM D955 | 0.50-0.70 | % |
| | 吸水率 | 23°C, 24 hr | ASTM D570 | 0.15 | % |
| | | 平衡, 23°C, 50% RH | ASTM D570 | 0.32 | % |
| | 洛氏硬度 | M 计秤 | ASTM D785 | 73 | |
| | | R 计秤 | ASTM D785 | 118 | |
| 机械性能 | 拉伸模量 | | ASTM D638 | 2410 | MPa |
| | 抗张强度 | 屈服, 23°C 2 | ASTM D638 | 60.0 | MPa |
| | | 断裂 | ASTM D638 | 71.0 | MPa |
| | 伸长率 | 屈服 | ASTM D638 | 6.0 | % |
| | | 断裂 | ASTM D638 | 150 | % |
| | 弯曲模量 | | ASTM D790 | 2410 | MPa |
| | 弯曲强度 | | ASTM D790 | 96.5 | MPa |
| | 耐磨耗性 | Change in Haze
(1000 g; CS-10 F wheel;
500 cycles) | ASTM D1044 | 45 | % |
| | 悬壁梁缺口冲击强度 3 | 23°C, 3.18 mm | ASTM D256 | 910 | J/m |
| | 无缺口悬臂梁冲击 | 23°C | ASTM D256 | 无断裂 | |
| | 装有测量仪表的落镖冲击 4 | 23°C, 3.18 mm, Total Energy | ASTM D3763 | 87.0 | J |
| 热性能 | 热变形温度 | 0.45 MPa, 退火, 4.00 mm | ASTM D648 | 144 | °C |
| | | 1.8 MPa,未退火, 4.00 mm | ASTM D648 | 128 | °C |
| | | 1.8 MPa, 退火, 4.00 mm | ASTM D648 | 141 | °C |
| | 维卡软化温度 |
| ASTM D1525 5 | 149 | °C |
| | 球压温度 6 | | IEC 60598-1 | >125 | °C |
| | 线形膨胀系数 | 流动(-40 到 82°C) | ASTM D696 | 0.000068 | cm/cm/°C |
| 电气性能 | 体积电阻率 7 | 23°C | ASTM D257 | 2.0E+17 | ohm·cm |
| | 介电强度 | | ASTM D149 | 17 | kV/mm |
| | 介电常数 | 60 Hz | ASTM D150 | 3.00 | |
| | 耗散因数 | 60 Hz | ASTM D150 | 0.0010 | |
| | 漏电起痕指数 | 2.00 mm | IEC 60112 | 250 | V |
| 其它 | UL 阻燃等级 6 | 1.60 mm | UL 94 | V-2 | |
| | | 3.00 mm | UL 94 | V-2 | |
| | 热灯丝点火温度 | 2.00 mm, 5.0 sec | EC 60695-2-13 | 850 | °C |
| | 极限氧指数 6 | | ASTM D2863 | 26 | % |
| | UL 档案号 | |
| E93278 | |
| | 平均燃烧程度 6 | | ASTM D635 | 3 | cm |
| 光学性能 | 折射率 | | ASTM D542 | 1.586 | |
| | 透射率 | | ASTM D1003 | 89.0 | % |
| | 雾度 | | ASTM D1003 | 0.70-1.5 | % |
产品细节图