PBT/日本东丽/1101G-30 PBT 聚对苯二甲酸丁二醇酯
'
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTM D792 | 1.55 | |
| 吸水率 | 23℃,24hr | ASTM D570 | 0.07 | % |
| 机械性能 | 拉伸强度 | 23℃ | ASTM D638 | 145 | MPa |
| 伸长率 | 23℃ | ASTM D638 | 5 | % |
| 弯曲强度 | 23℃ | ASTM D790 | 195 | MPa |
| 弯曲模量 | 23℃ | ASTM D790 | 8.8 | Gpa |
| Izod缺口冲击强度 | 缺口 | 23℃ | ASTM D256 | 90 | J/M |
| 缺口 | -40℃ | ASTM D256 | 75 | J/M |
| 无缺口 | -40℃ | ASTM D256 | 35 | KJ/m2 |
| 无缺口 | 23℃ | ASTM D256 | 65 | KJ/m2 |
| 洛氏硬度 | | ASTM D785 | 91 | M |
| 摩擦系数 | - | 对金属 | ASTM D1894 | 0.15 | |
| - | 对本身 | ASTM D1894 | 0.19 | |
| 电气性能 | 体积电阻率 | | ASTM D257 | 2.5 | |
| 耐电压 | | ASTM D149 | 23 | MV/m |
| 介电常数 | - | 50Hz | ASTM D150 | 3.7 | |
| - | 106Hz | ASTM D150 | 3.0 | |
| 介电损耗正切值 | - | 50Hz | ASTM D150 | 0.002 | |
| - | 106Hz | ASTM D150 | 0.02 | |
| 电弧电阻系数 | | ASTM D495 | 120 | S |
| 热性能 | 热变形温度 | - | 0.45MPa | ASTM D648 | 220 | ℃ |
| - | 1.82Mpa | ASTM D648 | 217 | ℃ |
| 线膨胀系数 | | ASTM D696 | 2.0 | |
| 阻燃性 | | UL94 | HB | |
'