LCP/日本宝理/A422
'
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTM D792 | 1.68 | g/cm3 |
| 成型收缩率 | Flow | ASTM D955 | 0.02 | % |
| 成型收缩率 | Across Flow | ASTM D955 | -0.05 | % |
| 吸水率 | Equilibrium,23℃,50% RH | ASTM D570 | 0.02 | % |
| 洛氏硬度 | M-Scale | ASTM D785 | 81 | |
| 机械性能 | 拉伸模量 | 3.20mm | ASTM D638 | 17600 | MPa |
| 拉伸强度 | 3.20mm | ASTM D638 | 186 | MPa |
| 断裂伸长率 | 3.20mm | ASTM D638 | 1.9 | % |
| 弯曲模量 | 3.20mm | ASTM D790 | 16600 | MPa |
| 弯曲强度 | 3.20mm | ASTM D790 | 229 | MPa |
| 摩擦系数 | VS.Metal-Dynamic | ASTM D1894 | 0.22 | |
| 摩擦系数 | VS.Metal-Static | ASTM D1894 | 0.29 | |
| 缺口冲击强度 | | ASTM D256 | 166 | J/m |
| 电气性能 | 表面电阻率 | | ASTM D257 | 1.5E+16 | ohms |
| 体积电阻率 | | ASTM D257 | 1.6E+16 | ohm.cm |
| 绝缘强度 | 3.00mm | ASTM D149 | 7 | kV/mm |
| 介电常数 | 1000Hz | ASTM D150 | 5.9 | |
| 介电常数 | 1E+7Hz | ASTM D150 | 5.4 | |
| 损耗因子 | 1000Hz | ASTM D150 | 0.005 | |
| 损耗因子 | 1E+7Hz | ASTM D150 | 0.019 | |
| 耐电弧性 | | ASTM D495 | 146 | sec |
| 耐导电径迹性 | | UL 746 | 225 | V |
| 热性能 | 热变形温度 | 1.8MPa,未退火,3.20mm | ASTM D648 | 220 | ℃ |
| 流动方向线性热膨胀系数 | 50℃,3.00mm | ASTM D696 | 6.0E-6 | cm/cm/℃ |
| 垂直流动方向线性热膨胀系数 | 50℃,3.00mm | ASTM D696 | 0.000043 | cm/cm/℃ |
| 比热 | | ASTM C351 | 1600 | J/kg/℃ |
| 阻燃等级 | 0.400mm | UL 94 | V0 | |
| 阻燃等级 | 0.800mm | UL 94 | V0 | |
| 阻燃等级 | 1.60mm | UL 94 | V0 | |
'