| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能吸水率24小时@73°FASTM D-5700.250% |
| 熔体流动速率标称,260℃/5.0kgfASTM D-123824.0g/10min |
| 物理性能光泽度无纹理,60℃ASTM D-52394 |
| 比重ASMT D-7921.15 |
| 模具收缩率flow,0.125"ASTM D-99555-7in/inE-3 |
| 模具收缩率xflow,0.125"ASTM D-9555-7in/inE-3 |
| 机械性能洛氏硬度ASTM D-785110R Scale |
| 仪表控制抗冲击总能量73°FASTM D-3763420in-lbs |
| 仪表控制抗冲击总能量-22°FASTM D-3763270in-lbs |
| 屈服抗拉强度2.0in/minASTM D-6389000Psi |
| 屈服挠曲强度0.250"ASTM D-79012800Psi |
| 缺口伊佐德冲击值-22°FASTM D-2561.5ft-lb/in |
| 断裂拉伸伸长2.0in/minASTM D-63825.0% |
| 缺口伊佐德冲击值73°FASTM D-2566.0ft-lb/in |
| 挠曲模量0.05in/min,2"spanASTM D-790365000Psi |
| 热性能热膨胀系数flow,0°F-300°FASTM E-8314×10-5in/in°F |
| 热膨胀系数xflow,0°F-300°FASTM E-8314×10-5in/in°F |
| 热畸变温度264Psi,0.125ASTM D-648220deg°F |
| 热畸变温度66Psi,0.125",未退火ASTM D-648240deg°F |
| 导热率ASTM C-1770.25W/m-C |