Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistance. Excellent flow and impact balance together with the thin wall flame resistance and all color options make Cycoloy CX7240U an ideal candidate for a wide variety of thin wall applications. | ||||
总体 | ||||
材料状态 |
| |||
资料 1 |
| |||
UL 黄卡 2 |
| |||
搜索 UL 黄卡 |
| |||
供货地区 |
| |||
添加剂 |
| |||
性能特点 |
| |||
用途 |
| |||
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
比重 | |||
-- | 1.19 | g/cm³ | ASTM D792 |
-- | 1.20 | g/cm³ | ISO 1183 |
熔流率 (260°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
溶化体积流率(MVR) (260°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
收缩率 - 流动 (3.20 mm) | 0.40 到 0.60 | % | Internal Method |
吸水率 | ISO 62 | ||
饱和, 23°C | 0.20 | % | |
平衡, 23°C, 50% RH | 0.10 | % |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | |||
-- 3 | 2950 | MPa | ASTM D638 |
-- | 2530 | MPa | ISO 527-2/1 |
抗张强度 | |||
屈服 4 | 65.0 | MPa | ASTM D638 |
屈服 | 65.0 | MPa | ISO 527-2/50 |
断裂 4 | 58.0 | MPa | ASTM D638 |
断裂 | 50.0 | MPa | ISO 527-2/50 |
伸长率 | |||
屈服 4 | 4.1 | % | ASTM D638 |
屈服 | 4.0 | % | ISO 527-2/50 |
断裂 4 | 100 | % | ASTM D638 |
断裂 | 90 | % | ISO 527-2/50 |
弯曲模量 | |||
50.0 mm 跨距 5 | 2750 | MPa | ASTM D790 |
-- 6 | 2500 | MPa | ISO 178 |
弯曲强度 | |||
-- 6, 7 | 96.0 | MPa | ISO 178 |
屈服, 50.0 mm 跨距 5 | 104 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度 8 | ISO 179/1eA | ||
-30°C | 10 | kJ/m² | |
23°C | 20 | kJ/m² | |
悬壁梁缺口冲击强度 | |||
-30°C | 100 | J/m | ASTM D256 |
23°C | 500 | J/m | ASTM D256 |
-30°C 9 | 10 | kJ/m² | ISO 180/1A |
23°C 9 | 20 | kJ/m² | ISO 180/1A |
装有测量仪表的落镖冲击 (23°C, Total Energy) | 65.0 | J | ASTM D3763 |
热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度 | |||
0.45 MPa, 未退火, 3.20 mm | 100 | °C | ASTM D648 |
1.8 MPa, 未退火, 3.20 mm | 89.0 | °C | ASTM D648 |
1.8 MPa, 未退火, 6.40 mm | 99.0 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 10 | 93.0 | °C | ISO 75-2/Af |
维卡软化温度 | |||
-- | 106 | °C | ASTM D1525 11 |
-- | 110 | °C | ISO 306/B50 |
-- | 113 | °C | ISO 306/B120 |
Ball Pressure Test (75°C) | Pass |
| IEC 60695-10-2 |
线形膨胀系数 | |||
流动 : -40 到 40°C | 0.000063 | cm/cm/°C | ASTM E831 |
流动 : -40 到 40°C | 0.000062 | cm/cm/°C | ISO 11359-2 |
横向 : -40 到 40°C | 0.000054 | cm/cm/°C | ASTM E831, ISO 11359-2 |
RTI Elec | 90.0 | °C | UL 746 |
RTI Imp | 90.0 | °C | UL 746 |
RTI Str | 90.0 | °C | UL 746 |
电气性能 | 额定值 | 单位制 | 测试方法 |
相比耐漏电起痕指数(CTI) | PLC 3 |
| UL 746 |
高电弧燃烧指数(HAI) | PLC 0 |
| UL 746 |
热丝引燃 (HWI) | PLC 3 |
| UL 746 |
可燃性 | 额定值 | 单位制 | 测试方法 |
UL 阻燃等级 | UL 94 | ||
0.400 mm | V-2 |
| |
0.600 mm | V-1 |
| |
0.750 mm | V-0 |
| |
1.50 mm | 5VB |
| |
3.00 mm | 5VA |
| |
灼热丝易燃指数 (0.750 mm) | 960 | °C | IEC 60695-2-12 |
热灯丝点火温度 | IEC 60695-2-13 | ||
1.00 mm | 825 | °C | |
3.00 mm | 800 | °C |
注射 | 额定值 | 单位制 |
|
干燥温度 | 90.0 | °C | |
干燥时间 | 4.0 | hr | |
建议的最大水分含量 | 0.040 | % | |
建议注入量 | 40 到 80 | % | |
料筒温度 | 60.0 到 80.0 | °C | |
螺筒后部温度 | 260 到 300 | °C | |
螺筒中部温度 | 260 到 300 | °C | |
螺筒前部温度 | 265 到 300 | °C | |
射嘴温度 | 265 到 300 | °C | |
加工(熔体)温度 | 270 到 300 | °C | |
模具温度 | 60.0 到 90.0 | °C | |
背压 | 0.300 到 0.700 | MPa | |
螺杆转速 | 40 到 70 | rpm | |
排气孔深度 | 0.038 到 0.076 | mm |