性能 Properties | 测试条件 Test Condition | 单位 Units | 标准 Standards | 电镀级 Plating | 耐热和汽车应用 High Heat and Automotive Applications |
377 | H701 | H802 | H950 |
流变性能/Rheological Properties |
熔融指数 Melt flow index | 220℃;10kg | g/10min | ISO 1133 | 28 | 9 | 8 | 4 |
成型收缩率 Moulding shrinkage | % | ISO 294-4 | 0.4-0.6 | 0.5-0.8 | 0.4-0.7 | 0.5-0.7 |
机械性能/Mechanical Properties |
屈服应力 Yield stress | 50mm/min | MPa | ISO 527 | 48 | 41 | 50 | 49 |
拉伸强度 Tensile stress @ break | 50mm/min | MPa | ISO 527 | 34 | - | - | - |
断裂延伸率 Tensile strain @ break | 50mm/min | % | ISO 527 | 20 | >15 | >15 | >15 |
拉伸模量 Tensile modulus | 1mm/min | MPa | ISO 527 | 2500 | 2150 | 2700 | 2600 |
弯曲强度 Flexural strength | 2mm/min 80 x 10 x 4 | MPa | ISO 178 | 71 | 65 | 80 | 80 |
弯曲模量 Flexural strength | 2mm/min 80 x 10 x 4 | MPa | ISO 178 | 2400 | 2150 | 2700 | 2600 |
IZOD缺口冲击强度 IZOD notched impact strength | 23℃ -20℃ -30℃ | KJ/m2 | ISO 180/1A | 17 13 7 | 24 - 12 | 15 - 8 | 17 - 8 |
洛氏硬度 Rockwell hardness | t = 6.4mm | R Scale | ISO 2039-2 | 112 | 951) | 1151) | 1101) |
热性能/Thermal properties |
热变形温度:(退火处理*)方法Af Heat distortion temperature;(annealed*)method Af | 1.80MPa | ℃ | ISO 75 | 91 | 99 | 100 | 105 |
热变形温度:(退火处理*)方法Bf Heat distortion temperature;(annealed*)method Bf | 0.45MPa | ℃ | ISO 75 | 95 | 105 | 106 | 112 |
维卡软化温度 Vicat softening temperature | 50N;120℃/h | ℃ | ISO 306 | 98 | 1042) | 1092) | 1132) |
其它性能/Other properties |
密度 Density | | g/cm3 | ISO 1183 | 1.05 | 1.04 | 1.05 | 1.05 |
光泽度 Gloss | 60° | | | 90 | - | - | - |
可烧性试验UL94 Flammability UL94 | 厚度1.6mm thickness 1.6mm | 类别 Class | UL 94 | HB | HB | HB | HB |
*退火处理/Annealing:80℃,4h 1)球压痕硬度/Ball indentation hardness ISO 2309-1(N/mm2) 2)特使条件/Test Conditions:50N;50℃/h |
SAN 注射品级/Injection modulding grades
性能 Properties | 测试条件 Test Condition | 单位 Units | 标准 Standards | 通用品级 General Purpose | 特殊品级 Special Grade |
SAN C | SAN 51 |
流变性能/Rheological Properties |
熔融指数 Melt flow index | 220℃;10kg | g/10min | ISO 1133 | 23 | 15 |
成型收缩率 Moulding shrinkage | % | ISO 294-4 | 0.3-0.4 | 0.3-0.4 |
机械性能/Mechanical Properties |
屈服应力 Yield stress | 50mm/min | MPa | ISO 527 | 68 | 76 |
断裂延伸率 Tensile strain @ break | 50mm/min | % | ISO 527 | 3.2 | 3.8 |
拉伸模量 Tensile modulus | 1mm/min | MPa | ISO 527 | 3700 | 3800 |
弯曲强度 Flexural strength | 2mm/min 80 x 10 x 4 | MPa | ISO 178 | 111 | 125 |
弯曲模量 Flexural strength | 2mm/min 80 x 10 x 4 | MPa | ISO 178 | 3800 | 3900 |
IZOD缺口冲击强度 IZOD notched impact strength | 23℃ | KJ/m2 | ISO 180/1A | 2 | 2 |
洛氏硬度 Rockwell hardness | t = 6.4mm | R Scale | ISO 2039-2 | 126 | 126 |
热性能/Thermal properties |
热变形温度:(退火处理*)方法Af Heat distortion temperature;(annealed*)method Af | 1.80MPa | ℃ | ISO 75 | 101 | 102 |
热变形温度:(退火处理*)方法Bf Heat distortion temperature;(annealed*)method Bf | 0.45MPa | ℃ | ISO 75 | 103 | 104 |
维卡软化温度 Vicat softening temperature | 50N;120℃/h | ℃ | ISO 306 | 104 | 106 |
其它性能/Other properties |
密度 Density | | g/cm3 | ISO 1183 | 1.08 | 1.08 |
可烧性试验UL94 Flammability UL94 | 厚度1.6mm thickness 1.6mm | 类别 Class | UL 94 | HB | HB |
'