混合高抗冲聚苯乙烯 GPPS/美国陶氏/PS121 聚苯乙烯 透明gpps
产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
熔体流动速率 | 200℃/5kg | ASTM D-1238 | 7 | g/10min |
比重 | | ASTM D-792 | 1.04 | g/cm3 |
模具收缩率 | | ASTM D-955 | 0.004-0.007 | cm/cm |
拉伸屈服强度 | | ASTM D-638 | 48 | MPa |
拉伸断裂强度 | | ASTM D-638 | 48 | MPa |
断裂伸长率 | | ASTM D-638 | 2 | % |
弯曲强度 | | ASTM D-790 | 90 | MPa |
弯曲模量 | | ASTM D-790 | 3241 | MPa |
IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 16 | J/m |
线性膨胀系数 | 10-5 | | 7.6 | cm/cm/℃ |
阻燃等级 | 1.5mm | UL 94 | HB |
维卡软化点 | | ASTM D-1525 | 99 | ℃ |
热变形温度 | 1.82MPa,未经退火 | ASTM D-648 | 76 | ℃ |
热变形温度 | 1.82MPa,经退火 | ASTM D-648 | 94 | ℃ |