注塑级 GPPS/美国陶氏/680A 透明gpps 聚苯乙烯 塑料gpps
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔融流动速率 | 200℃/5kg | ASTM D-1238 | 8.5 | g/10min |
| 比重 | | ASTM D-792 | 1.04 | g/cm3 |
| 械具收缩率 | | ASTM D-955 | 0.004-0.007 | cm/cm |
| 拉伸屈服强度 | 压缩成型(注塑) | ASTM D-638 | 40.0(46.9) | MPa |
| 最终拉伸强度 | 压缩成型(注塑) | ASTM D-638 | 40.0(46.9) | MPa |
| 断裂伸长率 | 压缩成型(注塑) | ASTM D-638 | 1.0(2.0) | % |
| 弯曲模量 | 压缩成型(注塑) | ASTM D-790 | 3100(3190) | MPa |
| 弯曲强度 | 压缩成型(注塑) | ASTM D-790 | 56.5(89.6) | MPa |
| IZOD冲击强度 | 压缩成型(注塑) | ASTM D-256 | 10.7(16.0) | J/m |
| 热变形温度 | 264PSi，未退火 | ASTM D-648 | 82.8 | ℃ |
| 热变形温度 | 264PSi，退火 | ASTM D-648 | 102 | ℃ |
| 维卡软化点 | | ASTM D-1525 | 105 | ℃ |
| CLTE | | ASTM D-696 | 0.000076 | cm/cm℃ |
| 燃烧性 | 1.50mm | UL 94 | HB |