性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 |
机械性能 | 拉伸强度(引张强度) | | ASTM D638/ISO 527 | 450(6,380) | kg/cm²(MPa)[Lb/in2] |
断裂伸长率 | | ASTM D638/ISO 527 | - | % |
拉伸模量 | | ASTM D638/ISO 527 | - | kg/cm²(MPa)[Lb/in2] |
拉伸屈服伸长率(延伸率) | | ASTM D638/ISO 527 | 15 | % |
拉伸断裂伸长率(延伸率) | | ASTM D638/ISO 527 | - | % |
弯曲模量(弯曲弹性率) | | ASTM D790/ISO 178 | 22000(31000) | kg/cm²(MPa)[Lb/in2] |
弯曲强度 | | ASTM D790/ISO 178 | 650(9,200) | kg/cm²(MPa)[Lb/in2] |
洛氏硬度 | | ASTM D785 | R-112 | |
IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in |
1/4" -30℃ | ASTM D256/ISO 179 | 20(3.7) | kg·cm/cm(J/M)ft·lb/in |
1/8" 23℃ | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in |
1/8" -30℃ | ASTM D256/ISO 179 | 23(4.3) | kg·cm/cm(J/M)ft·lb/in |
Charpy冲击强度 | 23℃ (缺口) | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in |
-30℃(缺口) | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in |
23℃(无缺口) | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in |
-30℃(无缺口) | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in |
物性性能 | 比重(密度) | | ASTM D792/ISO 1183 | 1.03 | |
成型收缩率 | | ASTM D955 | - | % |
熔融指数(流动系数) | 200℃/5kg | ASTM D1238/ISO 1133 | - | g/10min |
220℃/10kg | ASTM D1238/ISO 1133 | 7.5 | g/10min |
吸水率 23℃/24H | | ASTM D570/ISO 62 | - | % |
热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | 107(225) | ℃(℉) |
未退火 | ASTM D648/ISO 75 | 97(207) | ℃(℉) |
维卡软化点 | | ASTM D1525/ISO R306 | 115(239) | ℃(℉) |
熔点 | | - | - | ℃(℉) |
燃烧性(率) | | UL94 | 1.6mmHB | |
线性膨胀系数 | | ASTM D696/ISO 11359 | - | mm/mm.℃ |
加工条件 | 干燥条件 | | | 90~95°C下烘料约3小时 | |
加工温度 | 射嘴 | | 220~250°C | ℃ |
料筒前段 | | 230~250 °C | ℃ |
料筒中段 | | 230~250 ° | ℃ |
料筒后段 | | 220~240 ° | ℃ |
熔体温度 | | | - | ℃ |
模具温度 | | | 30~70°C | ℃ |
压力 | 注塑压力 | | 50~70kg/cm² | Mpa |
保压压力 | | 40~60kg/cm² | Mpa |
背压 | | 5~15kg/cm² | Mpa |
螺杆转速 | | | - | rpm |
其他 | 备注 | 在射出周期中勿将热融胶长期停留在加热管中 |
颜色 | - |
特性 | 耐热性、高冲击强度 |
用途 | 发热家电外壳 / 乾发吹风筒 / 熨斗外壳 / 暖风机 / 汽车零配件如仪表板 / 水箱护罩等 |