性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
其它性能 | 吸水率(24hr) | | ASTM D-570 | 0.01 | % |
物理性能 | 密度 | | ASTM D-1505 | 0.835 | g/cm3 |
熔点 | | MCI方法 | 222 | ℃ |
熔融指数(260℃,5kg) | | ASTM D-1238 | 21 | g/10min |
机械性能 | 弹性模量 | | ASTM D-790 | 640 | MPa |
拉伸强度 | | ASTM D-638 | 18 | MPa |
断裂伸长率 | | ASTM D-638 | 60 | % |
弹性强度 | | ASTM D-790 | 25 | MPa |
屈服拉伸强度 | | ASTM D-638 | 25 | MPa |
Izod耐冲击强度 | | ASTM D-256 | 98 | KJ/m2 |
Rockwell硬度 | | ASTM D-785 | R62 | |
拉伸模量 | | ASTM D-638 | 785 | MPa |
电气性能 | 介电消散因子(23℃,1MHz) | | ASTM D-150 | 0.016 | |
介电强度 | | ASTM D-149 | 63 | KV/mm |
介电常数(100～1MHz) | | ASTM D-150 | 2.12 | |
体积电阻系数 | | ASTM D-257 | >1016 | Ωcm |
热性能 | 比热 | | ASTM C-351 | 0.47 | cal/g℃ |
热变形温度(4.6kg/cm2) | | ASTM D-648 | 75 | ℃ |
热传导系数 | | ASTM BS-847A | 4*10-4 | calcm/seccm2℃ |
燃烧速率 | | ASTM D-635 | 2.54 | cm/min |
线形膨胀系数 | | ASTM D-696 | 1.17*10-4 | 1/℃ |
模收缩率(纵向/横向) | | MCI方法 | 1.6/1.6 | % |
Vicat软化点 | | ASTM D-1525 | 151 | ℃ |
其它性能 | 透光率 | | ASTM D-1746 | 93 | % |
模糊度 | | ASTM D-1746 | 0.9 | % |
折射率 | | ASTM D-542 | 1.463 | nd |
TPX塑胶原料的性能：TPX的主要单体为4-甲基-1-戊烯(4-methyl-l-pentene)，为一无色，可燃的液体。与PP 或PE的单体比较，4-甲基-ｌ-戊烯为液体，较丙烯或乙烯(皆为气体)易于操作，其缺点为价格较高。4-甲基-1-戊烯具有刺激性，在高浓度下具有麻醉性，其沸点为54℃，熔点为- 154℃，自燃温度为300℃闪点为-7℃。由于闪点低，与热、火焰或氧化剂接触时有着火之危险性。4-甲基-l-戊烯是由丙烯台的二体化而制得。其反应是在钾处煤的作用下，于150～200℃及100大气压下进行。TPX塑胶原料的特性：TPX 的机械性质依其等级而定。一般常用的等级具有高屈服强度，但伸长率较低。α-烯烃含量较高的共聚合体的屈服强度较低，但伸长率高。一般来说，TPX 的强度与聚丙烯类似，但在较高的温度下，TPX 的机械性质较聚丙烯优异。TPX 具有相当高的软化点(Vicat 软化点可达170℃)，与聚丙烯比较，TPX 的耐温性较佳。TPX 的耐冲击强度与聚丙烯类似，较一般的透明性塑料如通用级聚苯乙烯及压克力树脂为高。整证来说，TPX 的机械性质可与通用速胶如聚丙烯、聚苯乙烯及聚氯乙烯等相比，但其耐温性较类似于一般的工程塑料如耐隆及聚碳酸脂等。 TPX塑胶原料的市场：TPX 的光学性质是相当特殊的特性。透明级TPX 的透明度可达90% 与通用级聚苯乙烯，压克力树脂及聚碳酸酯类似。此外，TPX 对紫外光的透明性亦相当优异。TPX 对紫外光的透明度较其它透明树脂如聚苯乙烯及压克力树脂为优，甚至比玻璃好，仅逊于石英玻璃。TPX 的耐化学品性优良，性质类似聚丙烯。与一些透明的塑料如聚苯乙烯，聚甲基丙烯酸甲酯及聚碳酸酯比较，TPX 的耐化学品性相当优异。TPX 具有优异的电绝缘性质。TPX 的介电常数是所有合成树脂中最低的一种，其介电损失性可与聚四乙烯(Teflon)及高密度聚乙烯(HDPE)相比。