PMMA/LG化学/HI835S
产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
基本性能 | 水吸收性 | 24h | ASTM D-570 | 0.4 | % |
物理性能 | 比重 | | ASTM D-792 | 1.17 | |
透明性 | 3.2mm | ASTM D-1003 | 91 | % |
反射指数 | | ASTM D-542 | 1.49 | |
机械性能 | 延伸率 | | ASTM D-638 | 67 | % |
洛氏硬度 | M-Scale | ASTM D-785 | 63 | |
弯曲模数 | | ASTM D-790 | 22400 | Kg/cm2 |
拉力 | | ASTM D-638 | 550 | Kg/cm2 |
弯曲强度 | | ASTM D-790 | 870 | Kg/cm2 |
冲击强度 | Izod Notched | ASTM D-256 | 4 | kg?cm/cm2 |
电气性能 | 功率系数 | 60Hz | ASTM D-150 | 0.04 | |
介电强度 | 4KV/S | ASTM D-149 | 15 | KV/mm |
抗体积系数 | | ASTM D-257 | >10 | Ω.cm |
介电定数 | 60Hz | ASTM D-150 | 3.5 | |
热性能 | 绵性膨胀系数 | | ASTM D-696 | 6×10-5 | cm/cm/°C |
热变形温度 | 18.6kg | ASTM D-648 | 91 | °C |
比热 | | | 0.35 | cal/g/°C |
维卡软化点 | 1kg | ASTM D-1525 | 101 | °C |
流动指数 | 230°C,3.8kg | ASTM D-1238 | 2.6 | g/10min |
热传导 | | ASTM D-177 | 5×10-4 | cal/seccm·°C/cm |
燃烧度 | | UL94 | HB | 1/8",1/16" |
模缩系数 | | ASTM D995-51 | 0.4-0.8 | % |