ABS/台湾台化/AG15A1
'
| 性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 |
| 机械性能 | 拉伸强度(引张强度) | | ASTM D638/ISO 527 | 510(50) | kg/cm²(MPa)[Lb/in2] |
| 断裂伸长率 | | ASTM D638/ISO 527 | | % |
| 拉伸模量 | | ASTM D638/ISO 527 | | kg/cm²(MPa)[Lb/in2] |
| 拉伸屈服伸长率(延伸率) | | ASTM D638/ISO 527 | | % |
| 拉伸断裂伸长率(延伸率) | | ASTM D638/ISO 527 | | % |
| 弯曲模量(弯曲弹性率) | | ASTM D790/ISO 178 | 27000(2650) | kg/cm²(MPa)[Lb/in2] |
| 弯曲强度 | | ASTM D790/ISO 178 | 850(84) | kg/cm²(MPa)[Lb/in2] |
| 洛氏硬度 | | ASTM D785 | R-110 | |
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | 20(196) | kg·cm/cm(J/M)ft·lb/in |
| 1/4" -30℃ | ASTM D256/ISO 179 | | kg·cm/cm(J/M)ft·lb/in |
| 1/8" 23℃ | ASTM D256/ISO 179 | | kg·cm/cm(J/M)ft·lb/in |
| 1/8" -30℃ | ASTM D256/ISO 179 | | kg·cm/cm(J/M)ft·lb/in |
| Charpy冲击强度 | 23℃ （缺口） | ASTM D256/ISO 179 | | kg·cm/cm(J/M)ft·lb/in |
| -30℃（缺口） | ASTM D256/ISO 179 | | kg·cm/cm(J/M)ft·lb/in |
| 23℃（无缺口） | ASTM D256/ISO 179 | | kg·cm/cm(J/M)ft·lb/in |
| -30℃（无缺口） | ASTM D256/ISO 179 | | kg·cm/cm(J/M)ft·lb/in |
| 物性性能 | 比重（密度） | | ASTM D792/ISO 1183 | 1.05 | |
| 成型收缩率 | | ASTM D955 | | % |
| 熔融指数（流动系数） | 200℃/5kg | ASTM D1238/ISO 1133 | 1.6 | g/10min |
| 220℃/10kg | ASTM D1238/ISO 1133 | 17 | g/10min |
| 吸水率 23℃/24H | | ASTM D570/ISO 62 | | % |
| 热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | 101 | ℃（℉） |
| 未退火 | ASTM D648/ISO 75 | 89 | ℃（℉） |
| 维卡软化点 | | ASTM D1525/ISO R306 | 104 | ℃（℉） |
| 熔点 | | - | | ℃（℉） |
| 燃烧性（率） | | UL94 | 1/16 | |
| 线性膨胀系数 | | ASTM D696/ISO 11359 | | mm/mm.℃ |
| 加工条件 | 干燥条件 | | | | |
| 加工温度 | 射嘴 | | | ℃ |
| 料筒前段 | | | ℃ |
| 料筒中段 | | | ℃ |
| 料筒后段 | | | ℃ |
| 熔体温度 | | | | ℃ |
| 模具温度 | | | | ℃ |
| 压力 | 注塑压力 | | | Mpa |
| 保压压力 | | | Mpa |
| 背压 | | | Mpa |
| 螺杆转速 | | | | rpm |
| 其他 | 备注 | |
| 颜色 | |
| 特性 | 特性：高光泽性，一般成型 |
| 用途 | 鞋跟，玩具，时钟外壳，音响外壳，手提箱 |
'