'Physical property Mechanical property Heat property Electrical property Molding property Optical property  

	Density	23℃	ISO1183	kg/m3	1050
	Specific Gravity		ASTM D792	-	1.05
	Tensile strength	23℃	ISO527-1,2	MPa	55
	Tensile strength		ASTM D638	MPa	51
	Tensile elongation at Break		ASTM D638	%	17
	Elongation at Break	23℃	ISO527-1,2	%	21
	Flexural Strength	23℃	ISO178	MPa	90
	Flexural Strength		ASTM D790	MPa	84
	Flexural Modulus	23℃/50%RH	ISO 178	MPa	2960
	Flexural Modulus		ASTM D790	MPa	2880
	Rockwell Hardness	23℃	ISO2039-2	R Scale	118
	Rockwell Hardness	23℃/50%RH	ASTM D785	Rスケール	118
	Charpy Impact Strength（Unnotched）	23℃	ISO179	kJ/m2	6
	Ball Pressure Temp./0.1mm Vicat Softening Temp.			℃	95〜95
	Izod Impact Strength（V-notched）	23℃ 12.7mm	ASTM D256	J/m	69
	Izod Impact Strength（V-notched）	0℃　12.7mm	ASTM D256	J/m	39
	Izod Impact Strength（V-notched）	-30℃ 12.7mm	ASTM D256	J/m	29
	Izod Impact Strength（V-notched）	23℃　3.2mm	ASTM D256	J/m	69
	Izod Impact Strength（V-notched）	0℃　3.2mm	ASTM D256	J/m	49
	Izod Impact Strength（V-notched）	-30℃ 3.2mm	ASTM D256	J/m	39
	Coef of Linear Thermal Expansion	−	ASTM D696	℃-1	0.000064
	Heat Deflection Temp High Load	1.80MPa	ISO75-1,2	℃	83
	Heat Deflection Temp(Unannealed)High Load	6.4mm/1.82MPa	ASTM D648	℃	87
	Flammability		UL94	rank/thickness mmt	HB
	Electrostatic Voltage	23℃,50%,24hr	Toray Method	V	-
	Half-life period of Electrostatic Voltage decay	23℃,50%,24hr	Toray Method	Sec.	-
	Surface Resistivity	23℃,50%,24hr	ASTM　D257	Ω	-
	Mold shrinkage	23℃/50%RH	Toray Method	%	0.4-0.6
	Melt Flow Rate	200℃/49N	ISO 1133	g/10min	-
	Melt Flow Rate	220℃/98N	ISO 1133	g/10min	25
	Melt Flow Rate	240℃/98N	ISO 1133	g/10min	-
	Gloss	an angle of incidence 60℃	Toray Method	%	-
	Total Light Transmission	23℃/50%RH　3mm thickness	ISO 13468	%	-
	Haze	23℃/50%RH　3mm thickness	ISO 14782	%	-

Applications of toyolac

• Generic Component/Livingware

• Electric home appliance

• Digital home appliance

'