材质
| 用途
| 化学成分
| 力学能力
| 线径（mm）
| 净重(kg)
| 阀芯直径(mm)
| 备注
|
ER304
| 主要用于焊接18Cr-8Ni钢
| C:0.064%
Mn:1.65%
Si:0.42%
Ni:8.33%
Cr:17.10%
| 拉伸强度Mpa 1200
| 0.08-0.45
| 5/10/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER304L
| 主要用于焊接17Cr-8Ni钢
| C:0.028%
Mn:1.65%
Si:0.42%
Ni:8.33%
Cr:17.10%
| 拉伸强度Mpa 1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER308
| 主要用于焊接19Cr-9Ni钢
| C:0.064%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:20.10%
| 拉伸强度Mpa 1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER308L
| 主要用于焊接20Cr-9Ni钢
| C:0.024%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:20.10%
| 拉伸强度Mpa 1200
| 0.8-4.5
| 5/12.5/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER309
| 主要用于焊接20Cr-13Ni钢
| C:0.064%
Mn:1.65%
Si:0.42%
Ni:14.33%
Cr:20.10%
| 拉伸强度Mpa 1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER309L
| 主要用于焊接20Cr-14Ni钢
| C:0.024%
Mn:1.65%
Si:0.42%
Ni:14.33%
Cr:20.10%
| 拉伸强度Mpa 1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER309Lsi
| 主要用于焊接20Cr-14Ni钢
| C:0.024%
Mn:1.65%
Si:1.02%
Ni:14.33%
Cr:20.10%
| 拉伸强度Mpa1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER321
| 主要用于焊接16Cr-7Ni钢
| C:0.064%
Mn:1.65%
Si:0.42%
Ni:8.33%
Cr:17.10%Ti0.73
| 拉伸强度Mpa 1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER347
| 主要用于焊接16Cr-9Ni钢
| C:0.064%
Mn:1.65%
Si:0.42%
Ni:9.33%
Cr:17.10%
（Ta+Nb）（10*C）-10
| 拉伸强度Mpa 1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300 0
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER347L
| 主要用于焊接17Cr-9Ni钢
| C:0.064%
Mn:1.65%
Si:0.42%
Ni:9.33%
Cr:17.10%
（Ta+Nb）（10*C）-10
| 拉伸强度Mpa 1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300 0
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER316
| 主要用于焊接16Cr-9Ni钢
| C:0.064%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:17.10%
Mo2.03
| 拉伸强度Mpa 1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER316L
| 主要用于焊接17Cr-9Ni钢
| C:0.064%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:17.10%
Mo2.03
| 拉伸强度Mpa 1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
ER310
| 主要用于焊接24Cr-19Ni钢
| C:0.064%
Mn:1.65%
Si:0.42%
Ni:20.33%
Cr:25.10%
| 拉伸强度Mpa 1200
| 0.08-4.5
| 5/10/15/20
| 100/270/300
| MIG:0.8-1.6
TIG:1.0-4.5
|
气保护焊用不锈钢焊丝 上海海焊公司
牌号 | 焊丝化学成分% | 使用说明 |
C | Si | Mn | S | P | Cr | Ni | 其它 |
|
ER309L不锈钢焊丝 | 0.03 | 0.60 | 1.80 | 0.008 | 0.015 | 24.0 | 13.0 |
| 焊接复合钢的第一层及异种钢 |
ER308L不锈钢焊丝 | 0.03 | 0.60 | 1.80 | 0.008 | 0.015 | 20.0 | 10.0 |
| 焊接304L钢和核电第二层 |
ER347L不锈钢焊丝 | 0.03 | 0.60 | 1.80 | 0.008 | 0.015 | 20.0 | 10.0 | Nb：0.30 | 焊接同类型焊Ti不锈钢 |
ER316L不锈钢焊丝 | 0.03 | 0.60 | 1.80 | 0.008 | 0.015 | 18.0 | 12.0 | Mo：2.3 | 焊接18Cr-12Ni-2Mo型不锈钢 |
ER410不锈钢焊丝 | 0.052 | 0.27 | 0.38 | 0.015 | 0.011 | 12.62 | 0.47 |
| 0Cr13型不锈钢焊接 |
H2Cr13不锈钢焊丝 | 0.16 | 0.31 | 0.38 | 0.008 | 0.015 | 13.0 | 0.45 | Mo：0.26 | 1Cr13型不锈钢焊接 |
ER430不锈钢焊丝 | 0.042 | 0.31 | 0.38 | 0.008 | 0.015 | 16.21 | 0.45 | Mo：0.26 | 同类型不锈钢焊接，也可用于碳钢和不锈钢的异种钢焊接 |
ER00Cr18Ni12MoN不锈钢焊丝 | 0.013 | 0.36 | 1.86 | 0.008 | 0.015 | 18.65 | 12.70 | Mo：2.25 | 尿素用钢316L、316N的焊接 |
ER316Cu不锈钢焊丝 | 0.013 | 0.45 | 1.87 | 0.008 | 0.015 | 18.35 | 13.92 | Mo：2.61 Cu：1.80 | 同类型不锈钢的焊接 |
ER309LNb不锈钢焊丝 | 0.013 | 0.32 | 1.82 | 0.008 | 0.015 | 24.32 | 13.19 | Nb：0.60 | 复合钢的第一层及异种钢焊接 |
ER309LMo不锈钢焊丝 | 0.016 | 0.37 | 1.76 | 0.008 | 0.015 | 23.76 | 13.27 | Mo：2.46 | 复合钢的第一层及异种钢焊接 |
ER310不锈钢焊丝 | 0.12 | 0.45 | 1.76 | 0.008 | 0.015 | 26.27 | 21.36 |
| 焊接高温下工作的同类型不锈钢 |
ER385不锈钢焊丝 | 0.011 | 0.37 | 1.86 | 0.006 | 0.010 | 20.21 | 25.37 | Mo：4.96 Cu：1.50 | 耐硫酸及氯化物腐蚀，S、P含量极低，不宜产生裂纹 |