Product No.

Zr02 Content (%)

Filament Diameter (µm)

Glass Density (g/cm3)

Size Content (%)

Moisture Content (%)

Stiffness (mm)

ARR-H

> 16.2

14

2.5-2.6

1.5 - 2.2

0.10

> 120

ARR-L

> 14.5

1.2 - 1.6

0.20

> 150

Technical Data (Zr02 content 14.5%)

AR Roving Specifications

Virgin Tensile Strength

1500 - 1700  Mpa

Roving Tex (g/km)

2400 tex

Industrial Standard Tensile Strength

800N

Roving Yields (yds/lb)

207

Young's Modulus of Elasticity

69580 Mpa

Strand Tex

64 tex

Specific Gravity

2.6

Number of strands/roving

about 36

Strain at breaking point (stand) %

In boiling saturated Ca(OH)2 solution for 4 hours, the strength left is 82%

Loss on Ignition (%)

1 - 2 %

Water uptake

< 0.2%

Approx Roving Weight

18 kg/roll (40 lbs)

Softening Temperature

800 degrees centigrade