- PMMA/HI835S/LG化学 生产企业： LG化学
①原料描述部分
规格级别外观颜色该料用途备注说明③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 水吸收性 | 24h | ASTM D-570 | 0.4 | % |
| 物理性能 | 比重 | | ASTM D-792 | 1.17 | |
| 透明性 | 3.2mm | ASTM D-1003 | 91 | % |
| 反射指数 | | ASTM D-542 | 1.49 | |
| 机械性能 | 延伸率 | | ASTM D-638 | 67 | % |
| 洛氏硬度 | M-Scale | ASTM D-785 | 63 | |
| 弯曲模数 | | ASTM D-790 | 22400 | Kg/cm2 |
| 拉力 | | ASTM D-638 | 550 | Kg/cm2 |
| 弯曲强度 | | ASTM D-790 | 870 | Kg/cm2 |
| 冲击强度 | Izod Notched | ASTM D-256 | 4 | kg?cm/cm2 |
| 电气性能 | 功率系数 | 60Hz | ASTM D-150 | 0.04 | |
| 介电强度 | 4KV/S | ASTM D-149 | 15 | KV/mm |
| 抗体积系数 | | ASTM D-257 | >10 | Ω.cm |
| 介电定数 | 60Hz | ASTM D-150 | 3.5 | |
| 热性能 | 绵性膨胀系数 | | ASTM D-696 | 6×10-5 | cm/cm/°C |
| 热变形温度 | 18.6kg | ASTM D-648 | 91 | °C |
| 比热 | | | 0.35 | cal/g/°C |
| 维卡软化点 | 1kg | ASTM D-1525 | 101 | °C |
| 流动指数 | 230°C,3.8kg | ASTM D-1238 | 2.6 | g/10min |
| 热传导 | | ASTM D-177 | 5×10-4 | m·°C/cm |
| 燃烧度 | | UL94 | HB | 1/8",1/16" |
| 模缩系数 | | ASTM D995-51 | 0.4-0.8 | % |
产品介绍
- 产品信息
- 产品名称：PMMA
中文名称:超细PMMA粉
英文名称:Poly(methyl methacrylate)
中文别名:超细聚甲基丙烯酸甲酯粉;聚甲基丙烯酸甲酯;PMMA;聚(甲基甲基丙烯酸酯)
光学级PMMA（聚甲基丙烯酸甲酯）因其优良的透光性、电绝缘性、后加工性等应用广泛，被誉为“塑料女王”。 PMMA高性能光学级液晶材料，主要应用液晶显示器导光板、光纤材料、太阳能光伏电池等高端市场，目前国内只有德国、日本、台湾少数几家外资企业在国内生产，20万吨左右的缺口仍主要靠进口来弥补。
粒子图片
PMMA塑料(有机玻璃) |
英文名称:Polymethyl Methacrylate | (聚甲基丙烯酸甲脂) |
比重:1.18克/立方厘米 成型收缩率:0.5-0.7% 成型温度：160-230℃ 干燥条件：70-90℃ 4小时 |
物料性能 | 透明性极好,强度较高,有一定的耐热耐寒性,耐腐蚀,绝缘性良好,综合性能超过聚苯乙烯,但质脆,易熔于有机溶剂,如作透光材料,其表面硬度稍低,容易擦花. | 适于制作透明绝缘零件和强度一般的零件. |
成型性能 | 1.无定形料,吸湿大,需干燥,不易分解,流动性中等,易发生填充不良,粘模,收缩,熔接痕等. |
2.宜高压注射,在不出现缺陷的条件下取高料温,高模温,以增加流动性,降低内应力,改善透明性及强度.模具浇注系统表面应光洁,脱模斜度大,顶出均匀.同时设排气口,以防出现起泡. |