- 化学成分 (48)
- 力学性能 (33)
- 热处理制度 (0)
- 物理性能 (1)
- 工艺性能及试验 (3)
- 使用性能和用途举例 (0)
- 代号与类型 (0)
序号指标范围值单位说明
| 质量等级为C级时 |
| 1 | Si ( Si ) | ≤ 0.6 | % | |
| 2 | Mn ( Mn ) | ≤ 2 | % | |
| 3 | V ( V ) | ≤ 0.12 | % | |
| 4 | Ti ( Ti ) | ≤ 0.2 | % | |
| 5 | Cr ( Cr ) | ≤ 1 | % | |
| 6 | Ni ( Ni ) | ≤ 0.8 | % | |
| 7 | Cu ( Cu ) | ≤ 0.8 | % | |
| 8 | N ( N ) | ≤ 0.15 | % | |
| 9 | Mo ( mo ) | ≤ 0.3 | % | |
| 10 | B ( B ) | ≤ 0.004 | % | |
| 11 | Als ( Als ) | ≥ 0.015 | % | |
| 12 | C ( C ) | ≤ 0.18 | % | |
| 13 | S ( S ) | ≤ 0.03 | % | |
| 14 | P ( P ) | ≤ 0.03 | % | |
| 质量等级为D级时 |
| 1 | Si ( Si ) | ≤ 0.6 | % | |
| 2 | Mn ( Mn ) | ≤ 2 | % | |
| 3 | Nb ( Nb ) | ≤ 0.11 | % | |
| 4 | V ( V ) | ≤ 0.12 | % | |
| 5 | Ti ( Ti ) | ≤ 0.2 | % | |
| 6 | Cr ( Cr ) | ≤ 1 | % | |
| 7 | Ni ( Ni ) | ≤ 0.8 | % | |
| 8 | Cu ( Cu ) | ≤ 0.8 | % | |
| 9 | N ( N ) | ≤ 0.15 | % | |
| 10 | Mo ( mo ) | ≤ 0.3 | % | |
| 11 | B ( B ) | ≤ 0.004 | % | |
| 12 | Als ( Als ) | ≥ 0.015 | % | |
| 13 | C ( C ) | ≤ 0.18 | % | |
| 14 | S ( S ) | ≤ 0.025 | % | |
| 15 | P ( P ) | ≤ 0.03 | % | |
| 质量等级为E级时 |
| 1 | Si ( Si ) | ≤ 0.6 | % | |
| 2 | Mn ( Mn ) | ≤ 2 | % | |
| 3 | Nb ( Nb ) | ≤ 0.11 | % | |
| 4 | V ( V ) | ≤ 0.12 | % | |
| 5 | Ti ( Ti ) | ≤ 0.2 | % | |
| 6 | Cr ( Cr ) | ≤ 1 | % | |
| 7 | Ni ( Ni ) | ≤ 0.8 | % | |
| 8 | Cu ( Cu ) | ≤ 0.8 | % | |
| 9 | N ( N ) | ≤ 0.15 | % | |
| 10 | Mo ( mo ) | ≤ 0.3 | % | |
| 11 | B ( B ) | ≤ 0.004 | % | |
| 12 | Als ( Als ) | ≥ 0.015 | % | |
| 13 | C ( C ) | ≤ 0.18 | % | |
| 14 | S ( S ) | ≤ 0.02 | % | |
| 15 | P ( P ) | ≤ 0.025 | % | |
| 质量等级为1C级时 |
| 1 | Nb ( Nb ) | ≤ 0.11 | % | |
| 公称直径边长或厚度为≤ 63mm时 |
| 1 | 碳当量 ( CE ) | ≤ 0.49 * | % | 热机轧制或热机轧制加回火状态交货钢材 |
| 公称直径边长或厚度为63 ~ 120mm时 |
| 1 | 碳当量 ( CE ) | ≤ 0.49 * | % | 热机轧制或热机轧制加回火状态交货钢材 |
| 公称直径边长或厚度为120 ~ 250mm时 |
| 1 | 碳当量 ( CE ) | ≤ 0.49 * | % | 热机轧制或热机轧制加回火状态交货钢材 |