序号指标范围值单位说明
|
| 脱氧方法为F-沸腾钢;等级为A时 |
| 1 | Si ( Si ) | ≤ 0.35 | % | |
| 2 | Mn ( Mn ) | ≤ 1.4 | % | |
| 3 | Cr ( Cr ) | ≤ 0.3 | % | |
| 4 | Ni ( Ni ) | ≤ 0.3 | % | |
| 5 | Cu ( Cu ) | ≤ 0.3 | % | |
| 6 | C ( C ) | ≤ 0.22 | % | |
| 7 | S ( S ) | ≤ 0.05 | % | |
| 8 | P ( P ) | ≤ 0.045 | % | |
| 脱氧方法为Z-镇静钢;等级为A时 |
| 1 | Si ( Si ) | ≤ 0.35 | % | |
| 2 | Mn ( Mn ) | ≤ 1.4 | % | |
| 3 | Cr ( Cr ) | ≤ 0.3 | % | |
| 4 | Ni ( Ni ) | ≤ 0.3 | % | |
| 5 | Cu ( Cu ) | ≤ 0.3 | % | |
| 6 | C ( C ) | ≤ 0.22 | % | |
| 7 | S ( S ) | ≤ 0.05 | % | |
| 8 | P ( P ) | ≤ 0.045 | % | |
| 脱氧方法为F-沸腾钢;等级为B时 |
| 1 | Si ( Si ) | ≤ 0.35 | % | |
| 2 | Mn ( Mn ) | ≤ 1.4 | % | |
| 3 | Cr ( Cr ) | ≤ 0.3 | % | |
| 4 | Ni ( Ni ) | ≤ 0.3 | % | |
| 5 | Cu ( Cu ) | ≤ 0.3 | % | |
| 6 | C ( C ) | ≤ 0.2 | % | |
| 7 | S ( S ) | ≤ 0.045 | % | |
| 8 | P ( P ) | ≤ 0.045 | % | |
| 脱氧方法为Z-镇静钢;等级为B时 |
| 1 | Si ( Si ) | ≤ 0.35 | % | |
| 2 | Mn ( Mn ) | ≤ 1.4 | % | |
| 3 | Cr ( Cr ) | ≤ 0.3 | % | |
| 4 | Ni ( Ni ) | ≤ 0.3 | % | |
| 5 | Cu ( Cu ) | ≤ 0.3 | % | |
| 6 | C ( C ) | ≤ 0.2 | % | |
| 7 | S ( S ) | ≤ 0.045 | % | |
| 8 | P ( P ) | ≤ 0.045 | % | |
| 脱氧方法为Z-镇静钢;等级为C时 |
| 1 | Si ( Si ) | ≤ 0.35 | % | |
| 2 | Mn ( Mn ) | ≤ 1.4 | % | |
| 3 | Cr ( Cr ) | ≤ 0.3 | % | |
| 4 | Ni ( Ni ) | ≤ 0.3 | % | |
| 5 | Cu ( Cu ) | ≤ 0.3 | % | |
| 6 | C ( C ) | ≤ 0.17 | % | |
| 7 | S ( S ) | ≤ 0.04 | % | |
| 8 | P ( P ) | ≤ 0.04 | % | |
| 脱氧方法为TZ-特殊镇静钢;等级为D时 |
| 1 | Si ( Si ) | ≤ 0.35 | % | |
| 2 | Mn ( Mn ) | ≤ 1.4 | % | |
| 3 | Cr ( Cr ) | ≤ 0.3 | % | |
| 4 | Ni ( Ni ) | ≤ 0.3 | % | |
| 5 | Cu ( Cu ) | ≤ 0.3 | % | |
| 6 | C ( C ) | ≤ 0.17 | % | |
| 7 | S ( S ) | ≤ 0.035 | % | |
| 8 | P ( P ) | ≤ 0.035 | % | |
序号指标范围值单位说明
|
| 检验项目为化学成分时 |
| 1 | 试验取样数量 | 1(每炉) | | |
| 2 | 试验取样方法 | GB/T 20066 | | |
| 3 | 试验方法 | GB/T 223系列标准、GB/T 4336 | | |
| 检验项目为拉伸时 |
| 1 | 试验取样数量 | 1 | | |
| 2 | 试验取样方法 | GB/T 2975 | | |
| 3 | 试验方法 | GB/T 228 | | |
| 检验项目为冷弯时 |
| 1 | 试验取样数量 | 1 | | |
| 2 | 试验取样方法 | GB/T 2975 | | |
| 3 | 试验方法 | GB/T 232 | | |
| 检验项目为冲击时 |
| 1 | 试验取样数量 | 3 | | |
| 2 | 试验取样方法 | GB/T 2975 | | |
| 3 | 试验方法 | GB/T 229 | | |
序号指标范围值单位说明|
| 1 | ISC ( ISC ) | U12352 * | | 数字代号 |
| 2 | ISC ( ISC ) | U12355 * | | 数字代号 |
| 3 | ISC ( ISC ) | U12358 * | | 数字代号 |
| 4 | ISC ( ISC ) | U12359 * | | 数字代号 |