供应PBT/日本宝理/2002/非增强PBT/连接器专用PBT/树脂PBT
'
比重 | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
吸水率 (23°C, 24 hr) | 0.20 | % | ISO 62 |
抗张强度 | | | |
-- | 51.0 | MPa | ASTM D638 |
-- | 60.0 | MPa | ISO 527-2 |
伸长率 | | | |
断裂 | > 200 | % | ASTM D638 |
断裂 | 100 | % | ISO 527-2 |
弯曲模量 | | | |
-- | 2540 | MPa | ASTM D790 |
-- | 2630 | MPa | ISO 178 |
弯曲强度 | | | |
-- | 93.0 | MPa | ASTM D790 |
-- | 95.0 | MPa | ISO 178 |
简支梁缺口冲击强度 | 3.4 | kJ/m² | ISO 179/1eA |
悬壁梁缺口冲击强度 (6.35 mm) | 34 | J/m | ASTM D256 |
反向缺口冲击 | 1800 | J/m | ASTM D256 |
热变形温度 | | | |
1.8 MPa, 未退火 | 78.0 | °C | ASTM D648 |
1.8 MPa, 未退火 | 70.0 | °C | ISO 75-2/A |
线形膨胀系数 | | | |
流动 3 | 0.00010 | cm/cm/°C | ASTM D696 |
流动: 23 到 55°C | 0.00011 | cm/cm/°C | No Standard |
横向 3 | 0.00010 | cm/cm/°C | ASTM D696 |
横向: 23 到 55°C | 0.00011 | cm/cm/°C | No Standard |
体积电阻率 | | | |
3.00 mm | 5.0E+16 | ohm·cm | ASTM D257 |
-- | 5.0E+16 | ohm·cm | IEC 60093 |
介电强度 | | | |
2.00 mm 4 | 14 | kV/mm | ASTM D149 |
3.00 mm | 14 | kV/mm | IEC 60243-1 |
耐电弧性 | 173 | sec | ASTM D495 |
UL 阻燃等级 | HB | | UL 94 |

'