| 产品说明 | ||||
UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Automotive lens applications. Medium viscosity. UV-stabilized. Transparent colors only. | ||||
| 总体 | ||||
材料状态 |
| |||
资料 1 |
| |||
UL 黄卡 2 |
| |||
搜索 UL 黄卡 |
| |||
供货地区 |
| |||
添加剂 |
| |||
性能特点 |
| |||
用途 |
| |||
外观 |
| |||
加工方法 |
| |||
多点数据 |
| |||
| 物理性能 | 额定值 | 单位制 | 测试方法 |
比重 | 1.20 | g/cm³ | ASTM D792 |
熔流率 (300°C/1.2 kg) | 11 | g/10 min | ASTM D1238 |
收缩率 - 流动 (3.20 mm) | 0.50 到 0.70 | % | Internal Method |
吸水率 (24 hr) | 0.15 | % | ASTM D570 |
室外适用性 | f1 |
| UL 746C |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
抗张强度 3 (屈服) | 62.1 | MPa | ASTM D638 |
伸长率 3 (断裂) | 130 | % | ASTM D638 |
弯曲模量 4 (50.0 mm 跨距) | 2340 | MPa | ASTM D790 |
弯曲强度 4 (屈服, 50.0 mm 跨距) | 96.5 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
悬壁梁缺口冲击强度 (23°C) | 800 | J/m | ASTM D256 |
装有测量仪表的落镖冲击 (23°C, Energy at Peak Load) | 63.8 | J | ASTM D3763 |
落锤冲击 (23°C) | 169 | J | Internal Method |
拉伸冲击强度 5 | 578 | kJ/m² | ASTM D1822 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度 (1.8 MPa, 未退火, | 132 | °C | ASTM D648 |
RTI Elec | 100 | °C | UL 746 |
RTI Imp | 100 | °C | UL 746 |
RTI Str | 100 | °C | UL 746 |
| 电气性能 | 额定值 |
| 测试方法 |
相比耐漏电起痕指数(CTI) | PLC 2 |
| UL 746 |
高电弧燃烧指数(HAI) | PLC 1 |
| UL 746 |
高电压电弧起痕速率 (HVTR) | PLC 2 |
| UL 746 |
热丝引燃 (HWI) | PLC 4 |
| UL 746 |
| 可燃性 | 额定值 |
| 测试方法 |
UL 阻燃等级 (1.47 mm) | HB |
| UL 94 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
透射率 (2540 µm) | 88.0 | % | ASTM D1003 |
| 注射 | 额定值 | 单位制 |
|
干燥温度 | 121 | °C | |
干燥时间 | 3.0 到 | hr | |
干燥时间，最大 | 48 | hr | |
建议的最大水分含量 | 0.020 | % | |
建议注入量 | 40 到 60 | % | |
螺筒后部温度 | 271 到 293 | °C | |
螺筒中部温度 | 282 到 304 | °C | |
螺筒前部温度 | 293 到 316 | °C | |
射嘴温度 | 288 到 310 | °C | |
加工（熔体）温度 | 293 到 316 | °C | |
模具温度 | 71.1 到 93.3 | °C | |
背压 | 0.345 到 0.689 | MPa | |
螺杆转速 | 40 到 70 | rpm | |
排气孔深度 | 0.025 到 0.076 | mm |