供应PC/沙伯基础(原GE)/945A-116/阻燃V0/高透明PC
'
比重 | 1.19 | g/cm³ | ASTM D792 |
熔流率 (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
收缩率 - 流动 (3.20 mm) | 0.60 到 0.80 | % | Internal Method |
拉伸模量 3 | 2270 | MPa | ASTM D638 |
抗张强度 4 | | | ASTM D638 |
屈服 | 62.0 | MPa | |
断裂 | 67.0 | MPa | |
伸长率 4 | | | ASTM D638 |
屈服 | 6.0 | % | |
断裂 | 130 | % | |
弯曲模量 5 (50.0 mm 跨距) | 2370 | MPa | ASTM D790 |
弯曲强度 5 (屈服, 50.0 mm 跨距) | 101 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 (23°C) | 800 | J/m | ASTM D256 |
装有测量仪表的落镖冲击 (23°C, Total Energy) | 79.0 | J | ASTM D3763 |
热变形温度 | | | ASTM D648 |
0.45 MPa, 未退火,
3.20 mm | 137 | °C | |
1.8 MPa, 未退火,
3.20 mm | 126 | °C | |
维卡软化温度 | 143 | °C | ASTM D1525 6 |
线形膨胀系数 | | | ASTM E831 |
流动: -40 到 40°C | 0.000068 | cm/cm/°C | |
横向: -40 到 40°C | 0.000074 | cm/cm/°C | |
RTI Elec | 130 | °C | UL 746 |
RTI Imp | 120 | °C | UL 746 |
RTI Str | 130 | °C | UL 746 |
'