销售防紫外线PC/美国GE/153R-111/无卤PC/挤出级PC/抗UV聚碳酸酯
'
比重 | | | ASTM D792 |
-- | 1.20 | g/cm³ | |
-- | 1.19 | g/cm³ | |
特定体积 | 0.835 | cm³/g | ASTM D792 |
熔流率(300°C/1.2 kg) | 2.5 | g/10 min | ASTM D1238 |
收缩率 - 流动(3.20 mm) | 0.50 到 0.70 | % | Internal Method |
吸水率 | | | ASTM D570 |
24 hr | 0.15 | % | |
平衡, 23°C | 0.35 | % | |
平衡, 100°C | 0.58 | % | |
洛氏硬度 | | | ASTM D785 |
M 计秤 | 70 | | |
R 计秤 | 118 | | |
抗张强度 2 | | | ASTM D638 |
屈服 | 62.1 | MPa | |
断裂 | 65.5 | MPa | |
伸长率 2 | | | ASTM D638 |
屈服 | 7.0 | % | |
断裂 | 110 | % | |
弯曲模量 3(50.0 mm 跨距) | 2340 | MPa | ASTM D790 |
弯曲强度 3(屈服, 50.0 mm 跨距) | 93.1 | MPa | ASTM D790 |
抗泰伯磨耗(1000 Cycles, 1000 g, CS-17 转轮) | 10.0 | mg | ASTM D1044 |
悬壁梁缺口冲击强度(23°C) | 750 | J/m | ASTM D256 |
无缺口悬臂梁冲击(23°C) | 3200 | J/m | ASTM D4812 |
落锤冲击(23°C) | 169 | J | ASTM D3029 |
拉伸冲击强度 4 | 630 | kJ/m² | ASTM D1822 |
热变形温度 | | | ASTM D648 |
0.45 MPa, 未退火, 6.40 mm | 138 | °C | |
1.8 MPa, 未退火, 6.40 mm | 132 | °C | |
维卡软化温度 | 157 | °C | ASTM D1525 5 |
线形膨胀系数 - 流动(-40 到 95°C) | 0.000068 | cm/cm/°C | ASTM E831 |
比热 | 1260 | J/kg/°C | ASTM C351 |
导热系数 | 0.19 | W/m/K | ASTM C177 |
体积电阻率 | > 1.0E+16 | ohm·cm | ASTM D257 |
介电强度(3.20 mm, in Air) | 15 | kV/mm | ASTM D149 |
介电常数 | | | ASTM D150 |
50 Hz | 3.17 | | |
60 Hz | 3.17 | | |
1 MHz | 2.96 | | |
耗散因数 | | | ASTM D150 |
50 Hz | 0.00090 | | |
60 Hz | 0.00090 | | |
1 MHz | 0.010 | | |
折射率 | 1.586 | | ASTM D542 |
透射率(2540 µm) | 88.0 | % | ASTM D1003 |
雾度(2540 µm) | 1.0 | % | ASTM D1003 |
'