注塑级ABS/韩国LG/AF-360
'
ABS/韩国LG/AF-360产品物性：
比重 | 1.19 | g/cm³ | ASTM D792 |
熔流率 (220°C/10.0 kg) | 26 | g/10 min | ASTM D1238 |
收缩率 - 流动 (3.20 mm) | 0.40 到 0.70 | % | ASTM D955 |
洛氏硬度 (R 计秤) | 98 | | ASTM D785 |
拉伸模量 3 (3.20 mm) | 2060 | MPa | ASTM D638 |
抗张强度 4 (屈服, 3.20 mm) | 36.3 | MPa | ASTM D638 |
伸长率 4 | | | ASTM D638 |
屈服, 3.20 mm | 5.0 | % | |
断裂, 3.20 mm | 20 | % | |
弯曲模量 5 (6.40 mm) | 2260 | MPa | ASTM D790 |
弯曲强度 5 (屈服, 6.40 mm) | 60.8 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 | | | ASTM D256 |
-30°C, 3.20 mm | 69 | J/m | |
-30°C, 6.40 mm | 59 | J/m | |
23°C, 3.20 mm | 180 | J/m | |
23°C, 6.40 mm | 150 | J/m | |
热变形温度 | | | ASTM D648 |
0.45 MPa, 未退火, 6.40 mm 6 | 85.0 | °C | |
0.45 MPa, 未退火, 6.40 mm 7 | 92.0 | °C | |
维卡软化温度 | 91.0 | °C | ASTM D1525 8 |
RTI Elec | 60.0 | °C | UL 746 |
RTI Imp | 60.0 | °C | UL 746 |
RTI Str | 60.0 | °C | UL 746 |
UL 阻燃等级 | | | UL 94 |
1.50 mm | V-0 | | |
2.00 mm | | | |
3.00 mm | | |
'