超韧PPS/日本宝理/1130A1/增强30%GF/超韧级PPS/聚苯硫醚
'
比重 | 1.57 | g/cm³ | ASTM D792, ISO 1183 |
收缩率 | | | No Standard |
横向流量:
2.00 mm | 0.60 | % | |
流量:
2.00 mm | 0.30 | % | |
吸水率 | | | |
23°C, 24 hr | 0.010 | % | ASTM D570 |
23°C, 24 hr | 0.030 | % | ISO 62 |
抗张强度 | | | |
-- | 185 | MPa | ASTM D638 |
-- | 170 | MPa | ISO 527-2 |
伸长率 | | | |
断裂 | 2.5 | % | ASTM D638 |
断裂 | 2.0 | % | ISO 527-2 |
弯曲模量 | | | |
-- | 10500 | MPa | ASTM D790 |
-- | 10000 | MPa | ISO 178 |
弯曲强度 | | | |
-- | 250 | MPa | ASTM D790 |
-- | 245 | MPa | ISO 178 |
简支梁缺口冲击强度 | 10 | kJ/m² | ISO 179/1eA |
悬壁梁缺口冲击强度 | 100 | J/m | ASTM D256 |
热变形温度 | | | |
1.8 MPa, 未退火 | 265 | °C | ASTM D648 |
1.8 MPa, 未退火 | 260 | °C | ISO 75-2/A |
线形膨胀系数 3 | | | ASTM D696, No Standard |
流动 | 0.000020 | cm/cm/°C | |
横向 | 0.000040 | cm/cm/°C | |
体积电阻率 | | | |
3.00 mm | 3.0E+16 | ohm·cm | ASTM D257 |
-- | 3.0E+16 | ohm·cm | IEC 60093 |
介电强度 | | | |
3.00 mm | 13 | kV/mm | ASTM D149 |
3.00 mm | 16 | kV/mm | IEC 60243-1 |
介电常数 | | | IEC 60250 |
1 kHz | 4.00 | | |
1 MHz | 4.00 | | |
耗散因数 | | | IEC 60250 |
1 kHz | 0.0010 | | |
1 MHz | 0.0020 | | |
耐电弧性 | 124 | sec | No Standard |
相比耐漏电起痕指数(CTI) | 150 | V | UL 746 |
漏电起痕指数 | 150 | V | IEC 60112, ASTM D3638 |
UL 阻燃等级 | V-0 | | UL 94 |
熔体粘度 | | | |
154°C, 1000 sec^-1 | 350 | Pa·s | ISO 11443 |
310°C, 1000 sec^-1 | 340 | Pa·s | No Standard |
'