供应SPS/日本出光/S932/增强30%GF/高流动性SPS/薄膜按键开关SPS
'
抗张强度 (屈服) | 105 | MPa | ASTM D638 |
伸长率 (屈服) | 2.1 | % | ASTM D638 |
弯曲模量 | 9500 | MPa | ASTM D790 |
弯曲强度 | 165 | MPa | ASTM D790 |
热变形温度 | | | ASTM D648 |
0.45 MPa, 未退火 | 265 | °C | |
1.8 MPa, 未退火 | 245 | °C | |
线形膨胀系数 - 流动 | 0.000025 | cm/cm/°C | ASTM D696 |
体积电阻率 | 1.0E+16 | ohm·cm | ASTM D257 |
介电强度 | 35 | kV/mm | ASTM D149 |
介电常数 (1 MHz) | 3.00 | | ASTM D150 |
耗散因数 (1 MHz) | 0.0020 | | ASTM D150 |
耐电弧性 | 120 | sec | ASTM D495 |
漏电起痕指数 | 400 | V | IEC 60112 |
UL 阻燃等级 (0.0313 mm) | V-0 | | UL 94 |
Notched Izod Impact, ASTM D256: 7 kJ/m²
Unnotched Izod Impact, ASTM D256: 25 kJ/m² |
干燥温度 | 120 到 150 | °C | |
干燥时间 | 2.0 到 5.0 | hr | |
螺筒后部温度 | 270 | °C | |
螺筒中部温度 | 280 | °C | |
螺筒前部温度 | 290 | °C | |
射嘴温度 | 290 | °C | |
加工（熔体）温度 | 310 | °C | |
模具温度 | 60.0 到 80.0 | °C |
'