韩国LG LUMID PA6/ABS HI5083A(W) MF8％ 高冲击
LUMID HI5006A(W)  | Physical property | | MSDS |  |
| Injection Molding, PA6/ABS | |
 | Application | | | Injection Molding, PA6/ABS, High Impact, Good Dimensional Stability |
| Feature | | | Pipe Fitting, Electrical and Electronic parts |
| Properties | | | ALL Metric SI British | | | Physical | Method | Condition | Unit | Value | Specific Gravity | ASTM D792 | 23℃ | - | 1.06 | Molding Shrinkage (Flow), 3.2mm | ASTM D955 | 23℃ | % | 0.8 ~ 1.2 | Water Absorption | ASTM D570 | - | % | 0.7 |
|
Mechanical | Method | Condition | Unit | Value | Tensile Strength, 3.2mm @ Yield | ASTM D638 | 50mm/min | ㎏/㎠ | 450 | Tensile Elongation, 3.2mm @ Break | ASTM D638 | 50mm/min | % | 100 | Flexural Strength, 3.2mm | ASTM D790 | 1.3mm/min | ㎏/㎠ | 600 | Flexural Modulus, 3.2mm | ASTM D790 | 1.3mm/min | ㎏/㎠ | 16,000 | IZOD Impact Strength, 3.2mm (Notched) | ASTM D256 | 23℃ | kg·cm/cm | 70 |
|
Thermal | Method | Condition | Unit | Value | Melting Temperature | ASTM D3418 | - | ℃ | 220 | Heat Deflection Temperature, 6.4mm (Unannealed) | ASTM D648 | 18.6kg | ℃ | 80 | ASTM D648 | 4.6kg | ℃ | 110 | Coefficient of Linear Thermal Expansion Flow | ASTM D696 | - | 10-5 m/m℃ | 8 |
|
Electrical | Method | Condition | Unit | Value | Dielectric Strength, 1mm | ASTM D149 | 23℃ | kV/mm | 26 | Dielectric Constant | ASTM D150 | 10E6Hz | - | 2.9 | Volume Resistivity | ASTM D257 | 23℃ | Ohm·m | 1.00E+15 |
|
|
| 1) The listed values should be used for referential purpose only. |
| |