10.5 MFR. Improved flame retardance. Super mold release.

Property

TYPICAL PROPERTIES (1)

MECHANICAL

Value

Unit

Standard

Tensile Stress, yld, Type I, 50 mm/min

630

kgf/cm²

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

700

kgf/cm²

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

7

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

130

%

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

980

kgf/cm²

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

23900

kgf/cm²

ASTM D 790

Hardness, Rockwell M

70

-

ASTM D 785

Hardness, Rockwell R

118

-

ASTM D 785

Taber Abrasion, CS-17, 1 kg

10

mg/1000cy

ASTM D 1044

IMPACT

Value

Unit

Standard

Izod Impact, unnotched, 23°C

326

cm-kgf/cm

ASTM D 4812

Izod Impact, notched, 23°C

81

cm-kgf/cm

ASTM D 256

Tensile Impact, Type S

589

cm-kgf/cm²

ASTM D 1822

Falling Dart Impact (D 3029), 23°C

1728

cm-kgf

ASTM D 3029

Instrumented Impact Energy @ peak, 23°C

650

cm-kgf

ASTM D 3763

THERMAL

Value

Unit

Standard

Vicat Softening Temp, Rate B/50

154

°C

ASTM D 1525

HDT, 0.45 MPa, 6.4 mm, unannealed

137

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

132

°C

ASTM D 648

CTE, -40°C to 95°C, flow

6.84E-05

1/°C

ASTM E 831

Specific Heat

1.25

J/g-°C

ASTM C 351

Thermal Conductivity

0.27

W/m-°C

ASTM C 177

Relative Temp Index, Elec

130

°C

UL 746B

Relative Temp Index, Mech w/impact

130

°C

UL 746B

Relative Temp Index, Mech w/o impact

130

°C

UL 746B

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.2

-

ASTM D 792

Specific Volume

0.83

cm³/g

ASTM D 792

Density

1.19

g/cm³

ASTM D 792

Water Absorption, 24 hours

0.15

%

ASTM D 570

Water Absorption, equilibrium, 23C

0.35

%

ASTM D 570

Water Absorption, equilibrium, 100°C

0.58

%

ASTM D 570

Mold Shrinkage, flow, 3.2 mm (5)

0.5 - 0.7

%

SABIC Method

Melt Flow Rate, 300°C/1.2 kgf

10.5

g/10 min

ASTM D 1238

OPTICAL

Value

Unit

Standard

Light Transmission, 2.54 mm

88

%

ASTM D 1003

Haze, 2.54 mm

1

%

ASTM D 1003

Refractive Index

1.586

-

ASTM D 542

ELECTRICAL

Value

Unit

Standard

Volume Resistivity

>1.E+17

Ohm-cm

ASTM D 257

Dielectric Strength, in air, 3.2 mm

14.9

kV/mm

ASTM D 149

Relative Permittivity, 50/60 Hz

3.17

-

ASTM D 150

Relative Permittivity, 1 MHz

2.96

-

ASTM D 150

Dissipation Factor, 50/60 Hz

0.0009

-

ASTM D 150

Dissipation Factor, 1 MHz

0.01

-

ASTM D 150

Hot Wire Ignition {PLC)

2

PLC Code

UL 746A

High Voltage Arc Track Rate {PLC}

2

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC}

1

PLC Code

UL 746A

Comparative Tracking Index (UL) {PLC}

2

PLC Code

UL 746A

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized, 94V-2 Flame Class Rating (3)

1.09

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating (3)

5.99

mm

UL 94

UV-light, water exposure/immersion

F2

-

UL 746C

Source GMD, last updated:2011/12/08

Processing

Parameter

Injection Molding

Value

Unit

Drying Temperature

120

°C

Drying Time

3 - 4

hrs

Drying Time (Cumulative)

48

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

295 - 315

°C

Nozzle Temperature

290 - 310

°C

Front - Zone 3 Temperature

295 - 315

°C

Middle - Zone 2 Temperature

280 - 305

°C

Rear - Zone 1 Temperature

270 - 295

°C

Mold Temperature

70 - 95

°C

Back Pressure

0.3 - 0.7

MPa

Screw Speed

40 - 70

rpm

Shot to Cylinder Size

40 - 60

%

Vent Depth

0.025 - 0.076

mm

Source GMD, last updated:2011/12/08

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.